镍铬钼合金在真空熔融CaCl2-20%CaF2盐中的腐蚀行为
Corrosion Behavior of Ni-Cr-Mo Alloy in Vacuum Melted CaCl2-20%CaF2 Salt
摘 要
采用浸没法腐蚀试验分别研究了00Cr16Ni75Mo2Ti和Hastelloy N两种镍铬钼合金在800℃真空熔融CaCl2-20%CaF2(质量分数)盐中的腐蚀行为.结果表明:两种合金的腐蚀质量损失均随时间的延长而增大,腐蚀速率均随时间的延长而减缓,试验初期Hastelloy N合金的腐蚀速率明显大于00Cr16Ni75Mo2Ti合金的;两种合金的腐蚀机理均主要为合金元素在熔盐中的选择性脱溶;析出相的不同是导致Hastelloy N合金腐蚀质量损失明显大于00Cr16Ni75Mo2Ti合金的主要原因.
Hastelloy N合金
熔盐腐蚀
选择性脱溶
00Cr16Ni75Mo2Ti alloy
Hastelloy N alloy
molten salt corrosion
selective dissolution
Abstract
The corrosion behaviors of two Ni-Cr-Mo alloys including 00Cr16Ni75Mo2Ti and Hastelloy N had been studied by immersion experiments in vaccum melted CaCl2-20wt%CaF2 salt at 800℃.The results show that the corrosion weight loss of the two alloys increased with the prolongation of time while the corrosion rate decreased.At the initial stage of the test the corrosion rate of the Hastelloy N alloy was obviously higher than that of 00Cr16Ni75Mo2Ti alloy.The main corrosion mechanisms of the two alloys both were the selective dissolution of alloying elements in the molten salt.The difference of the precipitated phases was the main cause which caused that the weight loss of the Hastelloy N alloy was significantly higher than that of 00Cr16Ni75Mo2Ti alloy.
中图分类号 TG172.6
所属栏目 试验研究
基金项目
收稿日期 2009/8/6
修改稿日期 2009/2/1
网络出版日期
作者单位点击查看
备注石照夏(1985-),女,内蒙古乌海人,硕士研究生.
引用该论文: SHI Zhao-xia,SONG Zhi-gang,ZHENG Wen-jie,XU Rui-dong,JI Xiang-min,FENG Han. Corrosion Behavior of Ni-Cr-Mo Alloy in Vacuum Melted CaCl2-20%CaF2 Salt[J]. Materials for mechancial engineering, 2010, 34(10): 9～13
石照夏,宋志刚,郑文杰,徐瑞东,季祥民,丰涵. 镍铬钼合金在真空熔融CaCl2-20%CaF2盐中的腐蚀行为[J]. 机械工程材料, 2010, 34(10): 9～13
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陆世英,康喜范.镍基及铁镍基耐蚀合金[M].北京:化学工业出版社,1989:179-180.
【2】郑晓光,张文奇,郭曼玖.几种钴基合金在Na2SO4-K2SO4混合盐中高温腐蚀行为[J].北京科技大学学报,1990,12(2):120-124.
【3】MASAOSHI K,TAKUYA N,AKIO S.Metallurgical study on corrosion of austenitic steels in molten salt LiF-BeF2(Flibe)[J].Journal of Nuclear Materials,2009,386/388:685-688.
【4】常晓亮,王旭,王兰芳.316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为[J].机械工程材料,2007,31(4):11-13.
【5】吕家欣,郑磊,张麦仓,等.镍基合金FGH95在熔融NaCl-Na2SO4中的腐蚀行为[J].金属学报,2009,45(2):204-210.
【6】冈毅民.高钼镍基合金在熔盐中脱溶腐蚀的研究[J].中国腐蚀与防护学报,1981,1(3):64-71.
【7】OLSON L C,AMBROSEK J W,SRIDHARAN K.Materials corrosion in molten LiF-NaF-KF salt[J].Journal of Fluorine Chemistry,2009,130:67-73.
【2】郑晓光,张文奇,郭曼玖.几种钴基合金在Na2SO4-K2SO4混合盐中高温腐蚀行为[J].北京科技大学学报,1990,12(2):120-124.
【3】MASAOSHI K,TAKUYA N,AKIO S.Metallurgical study on corrosion of austenitic steels in molten salt LiF-BeF2(Flibe)[J].Journal of Nuclear Materials,2009,386/388:685-688.
【4】常晓亮,王旭,王兰芳.316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为[J].机械工程材料,2007,31(4):11-13.
【5】吕家欣,郑磊,张麦仓,等.镍基合金FGH95在熔融NaCl-Na2SO4中的腐蚀行为[J].金属学报,2009,45(2):204-210.
【6】冈毅民.高钼镍基合金在熔盐中脱溶腐蚀的研究[J].中国腐蚀与防护学报,1981,1(3):64-71.
【7】OLSON L C,AMBROSEK J W,SRIDHARAN K.Materials corrosion in molten LiF-NaF-KF salt[J].Journal of Fluorine Chemistry,2009,130:67-73.
相关信息