Effects of Annealing and Coiling Temperature on Microstructure and Properties of 590 MPa Cold Rolling Hot Dip Galvanizing Dual Phase Steel Plates
摘 要
在实验室制备了590 MPa级冷轧热镀锌双相钢板,采用SEM、TEM和拉伸试验等方法考察了退火温度、卷取温度等工艺参数对该钢显微组织和力学性能的影响.结果表明:经750~820 ℃保温100 s退火后,可以获得抗拉强度615 MPa以上、伸长率高达21%的综合性能良好的钢板;随着退火温度的升高,抗拉强度和屈服强度都会增大,伸长率则以820 ℃退火的最好,其次是800 ℃退火的,而750 ℃和780 ℃退火的则差一些;热轧后650 ℃卷取的钢板经冷轧和热镀锌退火后,其强度明显高于690 ℃卷取的.
Abstract
590 MPa cold rolling hot dip galvanizing dual phase steel plates were prepared in laboratory.Effects of coiling temperature and annealing temperature on microstructure and mechanical properties of the plates were studied by means of SEM,TEM and tensile experiments.The results indicate that after annealing at 750-820 ℃ for 100 s,the steel plates could obtain good universal properties,that the tensile strength and elongation could reach above 615 MPa and 21%,respectively.The tensile strength and yield strength increased with the increase of annealing temperature.The best elongation could be obtained when annealing at 820 ℃ and the better was at 800 ℃,while the elongation was relative poor when the annealing temperatures were 750 ℃ and 780 ℃.When the coiling temperature was 650 ℃,the strength of the steel plate after cold rolling and hot dip galvanizing annealing was higher than that of coiling at 690 ℃.
中图分类号 TG142.1 TG156
所属栏目 试验研究
基金项目 “十一五”国家科技支撑计划项目(2006BAE03A06);北京市科技计划资助项目(D07010300700701)
收稿日期 2009/11/24
修改稿日期 2010/3/4
网络出版日期
作者单位点击查看
备注金光灿(1981-),女,辽宁营口人,博士研究生.
引用该论文: JIN Guang-can,ZHAO Ai-min,ZHAO Zheng-zhi,NIU Feng1,LIU Li. Effects of Annealing and Coiling Temperature on Microstructure and Properties of 590 MPa Cold Rolling Hot Dip Galvanizing Dual Phase Steel Plates[J]. Materials for mechancial engineering, 2010, 34(12): 13~15
金光灿,赵爱民,赵征志,牛枫,刘利. 退火和卷取温度对590MPa级冷轧热镀锌双相钢板组织与性能的影响[J]. 机械工程材料, 2010, 34(12): 13~15
被引情况:
【1】金光灿,李锦,罗一平, "部分奥氏体化和完全奥氏体化铁素体/马氏体双相钢的CCT曲线",机械工程材料 39, 27-32(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】唐荻.国外新型汽车用钢的技术要求及研究开发现状[J].钢铁,2005,40(6):1-5.
【2】康永林,邝霜,尹显东,等.汽车用双相钢板的开发与研究进展[J].汽车工艺与材料,2006(5):1-5.
【3】马鸣图,SHI M F.先进的高强度钢及其在汽车工业中的应用[J].钢铁,2004,39(7):68-72.
【4】焦书军,张红,郑建平.冷轧热镀锌双相钢成分设计模型化的研究[J].宝钢技术,2003(5):43-47.
【5】IWAMA T,KITANO F,NAGATAKI Y,et al.Development of galvannealed dual-phase ultra-high strength steel sheets with superior formability and spot-weldability[C].Chicago:Association for Iron and Steel Technology(AIST),2004.
【6】张继诚,符仁钰,张梅,等.相同成分DP钢和 TRIP钢部分力学性能的比较[J].热加工工艺,2006,35(22):13-16.
【7】马鸣图,吴宝榕.双相钢-物理和力学冶金[M].北京:冶金工业出版社,2009.
【2】康永林,邝霜,尹显东,等.汽车用双相钢板的开发与研究进展[J].汽车工艺与材料,2006(5):1-5.
【3】马鸣图,SHI M F.先进的高强度钢及其在汽车工业中的应用[J].钢铁,2004,39(7):68-72.
【4】焦书军,张红,郑建平.冷轧热镀锌双相钢成分设计模型化的研究[J].宝钢技术,2003(5):43-47.
【5】IWAMA T,KITANO F,NAGATAKI Y,et al.Development of galvannealed dual-phase ultra-high strength steel sheets with superior formability and spot-weldability[C].Chicago:Association for Iron and Steel Technology(AIST),2004.
【6】张继诚,符仁钰,张梅,等.相同成分DP钢和 TRIP钢部分力学性能的比较[J].热加工工艺,2006,35(22):13-16.
【7】马鸣图,吴宝榕.双相钢-物理和力学冶金[M].北京:冶金工业出版社,2009.
相关信息