电梯梯级链长轴销断裂原因分析
Fracture Analysis on Long Axle-Pin of Elevator Chain Lift
摘 要
某电梯梯级链长轴销在装配过程中发生了断裂,采用光学显微镜、扫描电子显微镜、直读光谱仪、能谱仪和显微硬度机等对断裂的轴销进行了宏观形貌、化学成分、硬度、显微组织和开裂面形貌分析,以找出断裂原因.结果表明:其断裂的主要原因是轴销表面存在磨削应力和淬火残余应力,并在氢的共同作用下,轴销表面产生了氢致延迟性开裂,随着时间的延长裂纹进一步扩展,导致了轴销在装配过程中断裂.
淬火残余应力
氢致延迟性开裂
电梯轴销
grinding stress
quenching residual stress
hydrogen ductile-brittle fracture
elevator axle-pin
Abstract
A elevator chain lift long axle-pin fractured in assembling process.In order to find out the failure causes,macro morphology,chemical composition,micro-hardness,microstructure and fracture morphology were analyzed by means of optical microscope,scanning electron microscope,photoelectric direct reading spectrometer,EDS and micro-hardness tester.The results show that the main fracture reasons were the grinding stress and quenching retained stress on the axle-pin surface.And with the cooperation of the stress and hydrogen,hydrogen ductile-brittle fracture occurred on the surface.With the prolongation of the time the crack grew,that led to the axle-pin fracture in the process of assembling.
中图分类号 TG115
所属栏目 失效分析
基金项目 上海市自然科学基金资助项目(09ZR1409900)
收稿日期 2010/1/16
修改稿日期 2010/10/13
网络出版日期
作者单位点击查看
备注王荣(1966-),男,陕西洛南人,教授级高级工程师,学士.
引用该论文: WANG Rong,GUO Chun-qiu. Fracture Analysis on Long Axle-Pin of Elevator Chain Lift[J]. Materials for mechancial engineering, 2010, 34(12): 74～76
王荣,郭春秋. 电梯梯级链长轴销断裂原因分析[J]. 机械工程材料, 2010, 34(12): 74～76
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】机械工业理化检验人员培训和资格鉴定委员会.金相检验[M].上海:上海科学普及出版社,2006:252.
【2】王广生,石康才,周敬恩,等.金属热处理缺陷分析及案例[M].北京:机械工业出版社,2007.
【3】任赞颂,张静江,陈质如,等.钢铁金相图谱[M].上海:上海科学技术文献出版社,2003.
【4】王荣.高强度螺栓断裂失效分析[J].物理测试,2008,26(2):50-54.
【5】郑文龙.钢的环境敏感断裂[M].北京:化学工业出版社,1988.
【2】王广生,石康才,周敬恩,等.金属热处理缺陷分析及案例[M].北京:机械工业出版社,2007.
【3】任赞颂,张静江,陈质如,等.钢铁金相图谱[M].上海:上海科学技术文献出版社,2003.
【4】王荣.高强度螺栓断裂失效分析[J].物理测试,2008,26(2):50-54.
【5】郑文龙.钢的环境敏感断裂[M].北京:化学工业出版社,1988.
相关信息