筋条参数对复合材料加筋壁板剪切承载能力的影响
Effects of Stiffener Parameters on Shear Carrying Capacity of Composite Stiffened Wall Panel
摘 要
通过对飞机上大量使用的复合材料加筋壁板进行剪切试验, 得到了不同筋条间距和腹板高度下加筋壁板的屈曲载荷和破坏载荷, 分析了筋条间距和腹板高度对加筋壁板剪切承载能力的影响。结果表明: 随着筋条间距增大, 加筋壁板由局部屈曲变为整体屈曲, 屈曲载荷和破坏载荷均逐渐减小; 随着腹板高度增大, 加筋壁板的屈曲载荷和破坏载荷均增大, 当腹板高度达到35 mm时则基本不再变化,分别保持在425 kN和775 kN左右。
加筋壁板
剪切载荷
屈曲载荷
破坏载荷
composite
stiffened wall panel
shearing load
buckling load
damage load
Abstract
Shearing test was carried on the composite stiffened wall panel widely used in aircraft, and buckling load and damage load of the stiffened wall panel were obtained at differe stiffener spacing and web height. The effects of stiffener spacing and web height on shear carrying capacity of the siffened wall panel were analyzed. Research show that the buckling form of the panel changed from local-buckling to overall-buckling and both the buckling load and damage load decreased with the increase of stiffener spacing. With the increase of web height, buckling load and damage load all increased and finally tended to certain value, the buckling load and damage load were about 425 kN and 775 kN, when the web height was up to 35 mm.
中图分类号 V258 DOI 10.11973/jxgccl201509011
所属栏目 材料性能及其应用
基金项目
收稿日期 2014/7/4
修改稿日期 2015/6/5
网络出版日期
作者单位点击查看
备注何吕龙(1990-), 男, 四川绵阳人, 硕士研究生。
引用该论文: HE Lü-long,SHANG Bo-lin,CHANG Fei,ZHANG Ya-hao. Effects of Stiffener Parameters on Shear Carrying Capacity of Composite Stiffened Wall Panel[J]. Materials for mechancial engineering, 2015, 39(9): 49～52
何吕龙,尚柏林,常飞,张亚豪. 筋条参数对复合材料加筋壁板剪切承载能力的影响[J]. 机械工程材料, 2015, 39(9): 49～52
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邵青, 何宇廷.复合材料加筋板剪切稳定性研究[J]. 航空精密制造技术, 2012,46(6): 46-48.
【2】谢紫龙, 尚柏林, 常飞,等. 分层损伤和完好复合材料薄壁加筋板的后屈曲承载能力及破坏形式[J].机械工程材料, 2013,37(7): 17-20.
【3】白瑞祥, 陈浩然, 刘远东.分层损伤复合材料加筋板屈曲和后屈曲性态研究[J].大连理工大学学报, 2003,43(3): 274-280.
【4】常飞, 尹俊杰, 李曙林,等. 损伤面积对复合材料加筋壁板剪切承载能力的影响[J].机械工程材料, 2013, 37(6): 14-21.
【5】YANG Xu, SHEN Zhen, YAN Ying, et al. New methodology for evaluating toughness of composite laminates investigation of damage resistance[J]. Chinese Journal of Aeronautics, 2003, 16(2):73-79.
【6】AMBUR D R, JAUNKY N, HILBURGER M W. Progressive failure studies of stiffened panels subjected to shear loading[J]. Composite Structures,2004,65(2):129-142.
【7】朱菊芬, 杨海平, 汪海.复合材料层合加筋板壳结构的后屈曲强度及破坏研究[J].航空学报, 1995, 16(1): 118-122.
【8】KONG C W, LEE I C, KIN C G, et al.Postbuckling and failure of stiffened composite panels under axial compression[J]. Composite Structures,1998,42(1):13-21.
【9】霍世慧, 王福生, 王佩艳, 等.复合材料机翼加筋壁板稳定性分析[J].应用力学学报,2010,27(2): 423-427.
【10】常楠, 杨伟, 赵美英.典型复合材料加筋壁板优化设计[J].机械设计,2007,24(12): 46-49.
【11】常楠, 刘江, 赵美英.复合材料蒙皮/长桁壁板结构优化设计[J].飞机设计,2007,27(6): 28-32.
【12】张朝晖, 刘嘉, 彭涛, 等.复合材料T型整体化结构的刚度简化方法[J].清华大学学报: 自然科学版,2011,51(12): 1882-1886.
【2】谢紫龙, 尚柏林, 常飞,等. 分层损伤和完好复合材料薄壁加筋板的后屈曲承载能力及破坏形式[J].机械工程材料, 2013,37(7): 17-20.
【3】白瑞祥, 陈浩然, 刘远东.分层损伤复合材料加筋板屈曲和后屈曲性态研究[J].大连理工大学学报, 2003,43(3): 274-280.
【4】常飞, 尹俊杰, 李曙林,等. 损伤面积对复合材料加筋壁板剪切承载能力的影响[J].机械工程材料, 2013, 37(6): 14-21.
【5】YANG Xu, SHEN Zhen, YAN Ying, et al. New methodology for evaluating toughness of composite laminates investigation of damage resistance[J]. Chinese Journal of Aeronautics, 2003, 16(2):73-79.
【6】AMBUR D R, JAUNKY N, HILBURGER M W. Progressive failure studies of stiffened panels subjected to shear loading[J]. Composite Structures,2004,65(2):129-142.
【7】朱菊芬, 杨海平, 汪海.复合材料层合加筋板壳结构的后屈曲强度及破坏研究[J].航空学报, 1995, 16(1): 118-122.
【8】KONG C W, LEE I C, KIN C G, et al.Postbuckling and failure of stiffened composite panels under axial compression[J]. Composite Structures,1998,42(1):13-21.
【9】霍世慧, 王福生, 王佩艳, 等.复合材料机翼加筋壁板稳定性分析[J].应用力学学报,2010,27(2): 423-427.
【10】常楠, 杨伟, 赵美英.典型复合材料加筋壁板优化设计[J].机械设计,2007,24(12): 46-49.
【11】常楠, 刘江, 赵美英.复合材料蒙皮/长桁壁板结构优化设计[J].飞机设计,2007,27(6): 28-32.
【12】张朝晖, 刘嘉, 彭涛, 等.复合材料T型整体化结构的刚度简化方法[J].清华大学学报: 自然科学版,2011,51(12): 1882-1886.
相关信息