湿拉拉拔速度对钢帘线用碳质量分数为0.92%镀铜钢丝性能的影响
Effects of Wet Drawn Speed on Property of 0.92wt.%C Brass-Plated Steel Wire Used for Steel Cord
摘 要
在相同的湿拉条件下对1.80 mm、0.92%碳(质量分数)的镀铜钢丝进行了不同速度的拉拔, 通过扭转分层仪、亨特疲劳试验机对湿拉至0.30 mm单丝的扭转分层性能以及亨特疲劳极限进行了测试。结果表明: 当湿拉速度高于13 m·s-1时, 单丝开始出现分层现象; 单丝扭转次数、亨特疲劳极限随着湿拉速度的提高呈下降趋势; 单丝性能下降的主要原因是由于随着湿拉速度的提升, 钢丝发热量逐渐增大, 渗碳体发生溶解所致。
扭转分层
亨特疲劳
镀铜钢丝
wet drawing
torsion and delamination
Hunter-type fatigue
brass-plated steel wire
Abstract
The 0.92wt.%C brass-plated steel wire with diameter of 1.80 mm was drawn at different drawing speeds under the same wet drawing conditions. The properties of the obtained filaments with diameter of 0.3 mm were studied by torsion & delamination test and Hunter-type fatigue test. The results showed that filament delamination occurred when the wet drawing speed exceeded 13 m·s-1. With the increase of wet drawn speed, the torsion value and Hunter-type fatigue limit dropped. The temperature of steel wire rose as the wet drawing speed increased, resulting in cementite dissolution, which is the main reason for property degradation of the filament.
中图分类号 TG113 DOI 10.11973/jxgccl201509015
所属栏目 材料性能及其应用
基金项目
收稿日期 2014/3/7
修改稿日期 2015/3/30
网络出版日期
作者单位点击查看
备注刘世军(1974-), 男, 江苏泰州人, 工程师。
引用该论文: LIU Shi-jun,QIAN Qing-sheng,ZHANG Zheng-yu,MEI Yi-dong,WANG Jian. Effects of Wet Drawn Speed on Property of 0.92wt.%C Brass-Plated Steel Wire Used for Steel Cord[J]. Materials for mechancial engineering, 2015, 39(9): 64～67
刘世军,钱庆生,张正裕,梅益东,王锏. 湿拉拉拔速度对钢帘线用碳质量分数为0.92%镀铜钢丝性能的影响[J]. 机械工程材料, 2015, 39(9): 64～67
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】罗奕文. 高强度ST/UT钢帘线在低滚动阻力轮胎中的应用[C]//2012中国橡胶年会. 北京:[出版者不详],2012:190-192.
【2】TASHIRO H, NISHIDA S, TARUI T, et al. Ultra high tensile strength steel cord[J]. Nippon-steel Techniacal Report, 1999,7(80):38-43.
【3】黄宝, 何立波, 高真凤, 等. 亚洲帘线钢线材生产现状及发展趋势[J]. 金属制品,2011,37(6):43-47.
【4】OKI Y, IBARAKI N, OCHIAI K. Microstructure influence on ultra high tensile steel cord fliament delamination[J]. Kobelco Technology Review, 2002, 25(8):35-38.
【5】钱庆生, 王秀丽, 刘世军, 等. 钢帘线用C92D2钢盘条的微观组织及力学性能[J]. 金属热处理,2013,38(11):29-33.
【6】TARUI T, MARUYAMA N, TAKAHASHI J, et al. Microstructure control and strengthening of high-carbon steel wires[J]. Nippon-steel Techniacal Report, 2005,1(91):56-61.
【7】张晓丹. 钢帘线钢丝冷拉拔过程中组织演变的定量研究与力学性能[D]. 北京:清华大学,2009.
【8】涂益友. 高速大应变冷拔钢丝的组织和力学性能[D]. 南京:东南大学,2006.
【9】刘波. 高碳钢丝及制品的塑性加工工艺与组织性能的研究[D]. 西安 :西安建筑科技大学,2004.
【10】董岩, 方峰, 蒋建清, 等. 高碳热轧盘条中的带状组织及其对拉丝变形行为的影响[J]. 机械工程材料,2005,29(8) :9-12.
【11】SHIMIZU K, KAWABE N. Size dependence of delamination of high-carbon steel wire[J]. ISIJ International, 2001,41(2):183-191.
【12】秦万信. 钢丝的高速拉拔[J]. 金属制品,1990,25(2):28-31.
【13】马明刚. 拉拔工艺及模具对钢丝力学性能的影响[D]. 贵阳:贵州大学,2006.
【14】ZHANG Zhi-bin. Estimate of endurance limits of steel cord under different bending fatigue conditions [J].Wire Journal International,2000,33(10) :116-119.
【15】LANGUILLAUME J, KAPELSKI G, BAUDELET B. Cementite dissolution in heavily cold drawn pearlitic steel wires[J]. Acta Materialia,1997,45(3):1201-1212.
【16】张晓丹, ANDREW G, 刘伟, 等.冷拉拔珠光体钢丝中渗碳体变形与溶解行为研究[J]. 金属热处理,2009,34(9):1-4.
【17】SUZUKI Y, ASAKAWA M, MIZUNO H, et al. Generating a mechanism of delamination in high carbon steel wire by experimental drawing[J]. Wire Journal International,2005(10):70-72.
【18】韩观昌, 程皖. 钢丝生产工艺装备(下)[M]. 北京:北京科技大学出版社,1988:88-100.
【2】TASHIRO H, NISHIDA S, TARUI T, et al. Ultra high tensile strength steel cord[J]. Nippon-steel Techniacal Report, 1999,7(80):38-43.
【3】黄宝, 何立波, 高真凤, 等. 亚洲帘线钢线材生产现状及发展趋势[J]. 金属制品,2011,37(6):43-47.
【4】OKI Y, IBARAKI N, OCHIAI K. Microstructure influence on ultra high tensile steel cord fliament delamination[J]. Kobelco Technology Review, 2002, 25(8):35-38.
【5】钱庆生, 王秀丽, 刘世军, 等. 钢帘线用C92D2钢盘条的微观组织及力学性能[J]. 金属热处理,2013,38(11):29-33.
【6】TARUI T, MARUYAMA N, TAKAHASHI J, et al. Microstructure control and strengthening of high-carbon steel wires[J]. Nippon-steel Techniacal Report, 2005,1(91):56-61.
【7】张晓丹. 钢帘线钢丝冷拉拔过程中组织演变的定量研究与力学性能[D]. 北京:清华大学,2009.
【8】涂益友. 高速大应变冷拔钢丝的组织和力学性能[D]. 南京:东南大学,2006.
【9】刘波. 高碳钢丝及制品的塑性加工工艺与组织性能的研究[D]. 西安 :西安建筑科技大学,2004.
【10】董岩, 方峰, 蒋建清, 等. 高碳热轧盘条中的带状组织及其对拉丝变形行为的影响[J]. 机械工程材料,2005,29(8) :9-12.
【11】SHIMIZU K, KAWABE N. Size dependence of delamination of high-carbon steel wire[J]. ISIJ International, 2001,41(2):183-191.
【12】秦万信. 钢丝的高速拉拔[J]. 金属制品,1990,25(2):28-31.
【13】马明刚. 拉拔工艺及模具对钢丝力学性能的影响[D]. 贵阳:贵州大学,2006.
【14】ZHANG Zhi-bin. Estimate of endurance limits of steel cord under different bending fatigue conditions [J].Wire Journal International,2000,33(10) :116-119.
【15】LANGUILLAUME J, KAPELSKI G, BAUDELET B. Cementite dissolution in heavily cold drawn pearlitic steel wires[J]. Acta Materialia,1997,45(3):1201-1212.
【16】张晓丹, ANDREW G, 刘伟, 等.冷拉拔珠光体钢丝中渗碳体变形与溶解行为研究[J]. 金属热处理,2009,34(9):1-4.
【17】SUZUKI Y, ASAKAWA M, MIZUNO H, et al. Generating a mechanism of delamination in high carbon steel wire by experimental drawing[J]. Wire Journal International,2005(10):70-72.
【18】韩观昌, 程皖. 钢丝生产工艺装备(下)[M]. 北京:北京科技大学出版社,1988:88-100.
相关信息