某井油管变扣短节断裂原因分析
Causes Analysis on the Fracture of the Tubing Joint in an Oil Well
摘 要
某井油管变扣短节服役5个月即发生断裂失效。通过对失效油管变扣短节的宏观形貌、微观形貌、理化性能进行分析和检验，查明了其断裂原因。结果表明:该油管变扣短节断裂主要是由硫化氢应力腐蚀开裂导致的；由于该井硫化氢含量较高，因此建议该井油管柱采用抗硫材料。
断裂
硫化物应力腐蚀开裂
tubing joint
fracture
sulfide stress corrosion cracking
Abstract
The tubing joint in an oil well fractured only used for five months, and the fracture reasons were analyzed by observing its macro and micro morphology and testing its physical and chemical properties. The results show that the fracture of the tubing joint was mainly caused by sulfide stress corrosion cracking. Because the hydrogen sulfide content in the oil well was rather high, sulfur resistant material was suggested to be used.
中图分类号 TE923 TG115 DOI 10.11973/lhjy-wl201510013
所属栏目 质量控制与失效分析
基金项目
收稿日期 2015/2/10
修改稿日期
网络出版日期
作者单位点击查看
备注王双来(1982-)，男，工程师，硕士。
引用该论文: WANG Shuang-lai,DU Zhi-jie,PENG Na. Causes Analysis on the Fracture of the Tubing Joint in an Oil Well[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(10): 730～732
王双来,杜志杰,彭娜. 某井油管变扣短节断裂原因分析[J]. 理化检验－物理分册, 2015, 51(10): 730～732
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】API Spec 5CT-2011套管和油管规范［S］.
【2】吕庆钢,陈磊,宋洪海.油管短节断裂失效分析［J］.金属热处理，2011,36(增刊): 11-12.
【3】吕拴录,袁鹏斌，吴天灵,等.73.0 mm EU J55油管短节断裂原因分析［J］.理化检验-物理分册，2008,44(12): 715-718.
【4】丁礼全，范植金，罗国华,等.45钢齿轮轴零件淬火开裂原因分析［J］.理化检验-物理分册，2008,50(10): 767-769.
【5】滕学清,吕栓录，徐永康,等.177.8 mm偏梯形螺纹套管粘扣原因分析［J］.理化检验-物理分册,2008,50(10): 780-784.
【2】吕庆钢,陈磊,宋洪海.油管短节断裂失效分析［J］.金属热处理，2011,36(增刊): 11-12.
【3】吕拴录,袁鹏斌，吴天灵,等.73.0 mm EU J55油管短节断裂原因分析［J］.理化检验-物理分册，2008,44(12): 715-718.
【4】丁礼全，范植金，罗国华,等.45钢齿轮轴零件淬火开裂原因分析［J］.理化检验-物理分册，2008,50(10): 767-769.
【5】滕学清,吕栓录，徐永康,等.177.8 mm偏梯形螺纹套管粘扣原因分析［J］.理化检验-物理分册,2008,50(10): 780-784.
相关信息