液化石油气储罐缺陷的超声波监测

液化石油气储罐缺陷的超声波监测

Ultrasonic Inspection of Liquefied Petroleum Gas Vessel

富阳

摘要

在役液化石油气储罐硫化物应力腐蚀开裂、氢鼓泡和氢致开裂等缺陷可能会扩展, 需要监控其扩展状况。介绍了针对这些不同类型缺陷的超声波监控方法, 总结了超声波监测过程中所必须注意的要点。

标签液化石油气

氢致开裂硫化物应力腐蚀开裂

氢鼓泡

氢致开裂

Liquefied petroleum gas

Sulfide stress corrosion crack

Hydrogen blister

Hydrogen induced crack

Abstract

Due to the fact that the defects of liquefied petroleum gas vessel in use, such as sulfide stress corrosion crack, hydrogen blister, hydrogen induced crack and so on, may spread, it was essential to inspect the spreading situation. The ultrasonic inspecting methods to the several defects were introduced, and the key points in inspecting process were summarized.

中图分类号 TG115.28

所属栏目试验研究

基金项目

收稿日期 2008/2/27

修改稿日期

网络出版日期

作者单位点击查看

备注富阳(1971-), 男, 高级工程师, 质检局超声波、磁粉和渗透检测Ⅲ级, 主要从事无损检测及特种设备检验方面的工作和研究。

引用该论文: FU Yang. Ultrasonic Inspection of Liquefied Petroleum Gas Vessel[J]. Nondestructive Testing, 2009, 31(2): 129～132
富阳. 液化石油气储罐缺陷的超声波监测[J]. 无损检测, 2009, 31(2): 129～132

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】TSG R7001—2004 压力容器定期检验规则[S].

【2】JB/T 4730.1~6—2005 承压设备无损检测[S].

相关信息

	标题	相关频次
	压力容器氢致开裂超声相控阵检测	3
	PE100管的室温单轴应变循环行为与棘轮效应	2
	裂纹圆棒法测PE100管材热熔对接接头的抗慢速裂纹扩展性能	2
	氢致开裂	2
	液化石油气储罐缺陷成因及处理方法	2
	在用蒸压釜磁粉检测的重点部位和常见错误	2
	10B21钢螺纹轴断裂失效分析	1
	16Mn低合金钢在H₂S环境中的氢损伤性能	1
	3Cr钢电阻焊小油管的性能	1
	42CrMoA钢制内齿圈开裂失效分析	1
	60Si2Mn弹簧钢力学性能不合格原因分析	1
	L360管线钢在普光气田集输系统的腐蚀	1
	SA516Gr70热轧容器钢板的氢渗透特征	1
	X70管线钢表面镍基合金堆焊层/母材界面的显微组织及氢致开裂行为	1
	采用声速法对高温部件进行定点测厚监测	1
	残极破碎机静刀刀具断裂的原因	1
	常减压水冷器小浮头螺栓断裂原因分析	1
	磁记忆技术在氢致开裂性能评价中的应用	1
	低碳钢氢致开裂声发射信号分析与模式识别	1
	低压环境中材料的氢损伤测试技术	1
	电化学充氢条件下夹杂物对管线钢氢致开裂敏感性的影响	1
	复合板压力容器裂纹的无损检测	1
	高强铝合金氢致开裂研究进展	1
	高压加热器管板与筒节环焊缝横向裂纹产生原因分析	1
	管道腐蚀评估技术与其检测方法对比	1
	管道氢致开裂失效机理	1
	晶粒度对35CrMo钢氢致开裂行为的影响	1
	抗硫套管钢P110SS在高含H₂S/CO₂、Cl^-共存条件下的腐蚀行为	1
	科研人员利用透射电镜破解氢致界面失效之谜	1
	连铸坯偏析对钢板氢致开裂的影响	1