Lamb Wave Testing of TaW Alloy Plates
摘 要
采用超声兰姆波检测方法, 和研制的1.25P15×20型38°入射角, 大晶片专用换能器, 对1.6 mm(厚)×80 mm(宽)的TaW合金板材实施了内部质量检测。试验表明, 该超声换能器不但可以稳定检出1.6 mm厚TaW 板材内 0.4 mm左右的缺陷, 而且孔径与兰姆波反射幅值呈现出良好的线性关系, 满足了生产中的质量控制要求。
Abstract
Aiming to evaluate inner quality of TaW alloy plates about 1.6 mm(thickness)×80 mm(width), using the manufactured 1.25P15×20 38° type ultrasonic transducer, the testing experiment has been actualized by lamb wave method. Its frequency was 1.25 MHz, an angle of incidence was 38°, and the size of wafer was 15 mm×20 mm. The sensitivity test results indicated that not only the defect about 0.4 mm in plate could be finded using this transducer, but also between the hole diameter and lamb wave amptitude was shown linear relation. It fulfilled quality demand of production.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2008/11/12
修改稿日期
网络出版日期
作者单位点击查看
备注王增勇(1971-), 男, 高级工程师, 从事金属材料及其构件的无损检测工艺及技术研究。
引用该论文: WANG Zeng-Yong,SUN Chao-Ming,LI Jian-Wen,LIU Zun-Wei. Lamb Wave Testing of TaW Alloy Plates[J]. Nondestructive Testing, 2009, 31(9): 689~690
王增勇,孙朝明,李建文,刘尊伟. 钽钨合金薄板的兰姆波检测[J]. 无损检测, 2009, 31(9): 689~690
被引情况:
【1】李建文,王增勇,孟玉堂, "TaW薄板分层缺陷检测及成因分析",无损检测 34, 32-34(2012)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张廷杰, 刘建章, 丁旭, 等.Ta-12W 合金的高温拉伸特性[J].稀有金属材料与工程,1999,28(6):345-348.
【2】GB/T 8651—2002 金属板材超声板波探伤方法[S].
【3】徐可北.金属薄板兰姆波检测技术[J].无损检测,1999,21(10):461-465.
【4】尚世同, 尚瑜娟.超声板波法在变厚度板检测中的应用[J].无损检测,1998,20(3):80-82,85.
【5】许可北, 张建合.复合材料层板泄漏兰姆波检测技术研究[J].无损检测,1999,21(11):505-508,511.
【2】GB/T 8651—2002 金属板材超声板波探伤方法[S].
【3】徐可北.金属薄板兰姆波检测技术[J].无损检测,1999,21(10):461-465.
【4】尚世同, 尚瑜娟.超声板波法在变厚度板检测中的应用[J].无损检测,1998,20(3):80-82,85.
【5】许可北, 张建合.复合材料层板泄漏兰姆波检测技术研究[J].无损检测,1999,21(11):505-508,511.
相关信息