复合材料拉伸过程的声发射特性研究
Research on Acoustic Emission Characteristics of The Composite Material during Tensile Test
摘 要
为了研究16MnR/0Cr18Ni9Ti复合材料断裂过程的声发射特性, 可以利用声发射技术对16MnR/0Cr18Ni9Ti复合材料试件的拉伸过程进行全程监测。研究表明, 材料拉伸断裂过程中, 声发射信号丰富明显, 可测性良好, 并且不同破坏阶段的声发射信号具有不同的特征。通过对不同拉伸阶段声发射信号的参数分析, 可以了解材料不同变形阶段的声发射特性, 并据此来分析材料损伤的发生、发展及演变过程。与传统的力学试验方法相比, 声发射技术在研究复合材料断裂过程方面具有明显的优势。
复合材料
拉伸
Acoustic emission
Composite material
Tensile
Abstract
To investigate the Acoustic Emission(AE) characteristics of 16MnR/0Cr18Ni9Ti composite material in the process of tensile failure, a whole tensile test of 16MnR/0Cr18Ni9Ti composite material can be monitored by AE technique. The test outcome indicates that the AE signal is abundant and has good measurability in the process. Besides, the AE signal at different tensile stages has different characteristics. Through parameters analysis of the AE signals acquired at each stage, the prominent AE characteristics of different tensile stages could be used to analyze the origination and propagation procedure of the material damage. Compared to traditional mechanical test, AE technique has obvious advantages in this aspect.
中图分类号 TG115.28
所属栏目 科研成果与学术交流
基金项目
收稿日期 2009/2/5
修改稿日期
网络出版日期
作者单位点击查看
备注丁利伟(1981-), 男, 助理工程师, 硕士研究生, 主要研究方向为声发射检测和红外探测。
引用该论文: DING Li-Wei,SHEN Yu-Di. Research on Acoustic Emission Characteristics of The Composite Material during Tensile Test[J]. Nondestructive Testing, 2009, 31(10): 781～785
丁利伟,沈玉娣. 复合材料拉伸过程的声发射特性研究[J]. 无损检测, 2009, 31(10): 781～785
被引情况:
【1】周伟,马力辉,张洪波,卢庆华, "风电叶片复合材料弯曲损伤破坏声发射监测",无损检测 33, 33-37(2011)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】方鹏, 成来飞, 张立同,等.C/SiC复合材料拉伸过程的声发射研究[J].无损检测,2006,28(7):358-361.
【2】Huguet S, Godin N, Gaertner R, et al. Use of acoustic emission to identify damage modes in glass fibre reinforced polyester[J]. Composites Science and Technology,2002,62(10/11):1433-1444.
【3】Siron O, Tsuda H. Acoustic emission in carbon fibre-reinforced plastic materials[J]. Annales de Chimie Science des Matériaux,2000,25(7):533-537.
【4】Xu T, Lei H, Xie C, et al. Investigation of impact fracture process with particle-filled polymer materials by acoustic emission[J]. Polymer Testing,2002,21(3):319-324.
【5】阳建红, 王芳文, 覃世勇.HTPB复合固体推进剂的声发射特性及损伤模型的实验和理论研究[J].固体火箭技术,2000,23(3):37-40.
【6】施昱, 陈 娟, 吴常红.16MnR/0Cr18Ni9复合钢板的焊接[J].工艺与新技术,2006,35(1):28-30.
【7】管家喜.保证15CrMo与0Cr18Ni9Ti异种钢接头焊接质量[J].化工质量,2001(4):38-40.
【8】谢希文.材料科学与工程导论[M].北京: 北京航空航天大学出版社,1991:120.
【9】刘国光, 程青蟾, 周丽绘,等.A3钢平板试样拉伸试验的声发射监测[J].上海金属,2003,25(3):32-37.
【2】Huguet S, Godin N, Gaertner R, et al. Use of acoustic emission to identify damage modes in glass fibre reinforced polyester[J]. Composites Science and Technology,2002,62(10/11):1433-1444.
【3】Siron O, Tsuda H. Acoustic emission in carbon fibre-reinforced plastic materials[J]. Annales de Chimie Science des Matériaux,2000,25(7):533-537.
【4】Xu T, Lei H, Xie C, et al. Investigation of impact fracture process with particle-filled polymer materials by acoustic emission[J]. Polymer Testing,2002,21(3):319-324.
【5】阳建红, 王芳文, 覃世勇.HTPB复合固体推进剂的声发射特性及损伤模型的实验和理论研究[J].固体火箭技术,2000,23(3):37-40.
【6】施昱, 陈 娟, 吴常红.16MnR/0Cr18Ni9复合钢板的焊接[J].工艺与新技术,2006,35(1):28-30.
【7】管家喜.保证15CrMo与0Cr18Ni9Ti异种钢接头焊接质量[J].化工质量,2001(4):38-40.
【8】谢希文.材料科学与工程导论[M].北京: 北京航空航天大学出版社,1991:120.
【9】刘国光, 程青蟾, 周丽绘,等.A3钢平板试样拉伸试验的声发射监测[J].上海金属,2003,25(3):32-37.
相关信息