Cr12MoV钢模具线切割开裂原因分析
Cracking Reason Analysis of Cr12MoV Steel Die during Spark Cutting
摘 要
采用断口观察、金相检验、化学成分分析、硬度检验等方法对Cr12MoV钢模具在线切割过程中产生开裂的原因进行了分析。结果表明:热处理工艺不当引起模具内的残余应力较大，加上线切割时导致模具内的残余应力重新分布，使模具在线切割时局部边缘产生超过材料抗拉强度的拉应力是导致模具开裂的主要原因; 另材料显微组织中的共晶碳化物最大尺寸严重超标，是导致该模具线切割时开裂的另一原因。
冷作模具钢
线切割
失效分析
Cr12MoV steel
cold working die steel
spark cutting
failure analysis
Abstract
By fracture surface observation, metallographic examination, chemical composition analysis and hardness test, the cracking reason of Cr12MoV steel die during spark cutting process was conducted. The results show that heat treatment induced big residual stress which redistributed during spark cutting was the main reason for the die cracking. Eutectic carbide size was out of limits, which made the die material easy to crack along eutectic carbide, was another reason.
中图分类号 TG142.45
所属栏目 质量控制与失效分析
基金项目 山东省科学院博士基金资助项目(2007.8)
收稿日期 2008/12/8
修改稿日期
网络出版日期
作者单位点击查看
备注吴晓峰(1976-),男,工学博士。
引用该论文: WU Xiao-feng,MA Kun,XU Na,SHI Jun-bo,LI Zhi-jun,ZANG Qi-shan4. Cracking Reason Analysis of Cr12MoV Steel Die during Spark Cutting[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(2): 128～130
吴晓峰,马 坤,徐 娜,时军波,李志军,臧启山. Cr12MoV钢模具线切割开裂原因分析[J]. 理化检验－物理分册, 2010, 46(2): 128～130
被引情况:
【1】斯松华,李智慧,徐震霖, "NSM30塑料模具钢板锯切开裂原因分析",理化检验－物理分册 51, 590-592(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】JB/T 7715-1995 冷锻模具用钢及热处理技术条件[S]．
【2】GB/T 14979-1994 钢的共晶碳化物不均匀度评定法[S]．
【3】JB/T 7713-1995 高碳高合金钢制冷作模具显微组织检验[S]．
【4】蔡美良. 新编工模具钢金相热处理[M]．北京: 机械工业出版社,1998: 65-66．
【5】上海交通大学编写组．金属断口分析[M]．北京: 国防工业出版社,1979: 116．
【6】王丽君,苗彬,孟先新．Cr12MoV钢不同热处理条件下的硬度和金相组织分析[J]．模具工业,2005(9): 52-56．
【2】GB/T 14979-1994 钢的共晶碳化物不均匀度评定法[S]．
【3】JB/T 7713-1995 高碳高合金钢制冷作模具显微组织检验[S]．
【4】蔡美良. 新编工模具钢金相热处理[M]．北京: 机械工业出版社,1998: 65-66．
【5】上海交通大学编写组．金属断口分析[M]．北京: 国防工业出版社,1979: 116．
【6】王丽君,苗彬,孟先新．Cr12MoV钢不同热处理条件下的硬度和金相组织分析[J]．模具工业,2005(9): 52-56．
相关信息