消化-澄清器开裂分析
Cracking Analysis of Slaker-classifier
摘 要
某304L奥氏体不锈钢消化-澄清器在试运行不久后即出现筒体开裂,发生泄漏事故。采用金相检验、扫描电镜及能谱分析等方法对开裂部位进行了分析。结果表明:消化-澄清器筒体开裂是由于蒸汽接管的振动,使器壁承受弯曲交变载荷;在交变载荷的作用下,消化-澄清器内、外壁萌生疲劳裂纹，疲劳裂纹不断扩展最终导致消化-澄清器发生疲劳开裂。
消化-澄清器
疲劳开裂
304L austenitic stainless steel
slaker-classifier
fatigue cracking
Abstract
The 304L austenitic stainless steel slaker-classifier cracked during the preoperation. By means of metallographical examination, SEM and EDS analysis, the cracked parts were analyzed.The results showed that the vibration of stream pipeline leading to an alternate loading on the wall of the slaker-classifier, caused the fatigue crack. With the extending of the crack, the slaker-classifier cracked finally.
中图分类号 TQ051.8
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/5/15
修改稿日期
网络出版日期
作者单位点击查看
备注孙 旭(1982-),男,硕士研究生。
引用该论文: SUN Xu,CHEN Jin,WANG Yin-pei. Cracking Analysis of Slaker-classifier[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(3): 204～206
孙 旭,陈 进,王印培. 消化-澄清器开裂分析[J]. 理化检验－物理分册, 2010, 46(3): 204～206
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴连生. 断口分析及其在失效分析中的应用[J]. 理化检验-物理分册,1994,30(5): 26-32．
【2】RADAJ D. 焊接结构疲劳强度[M]. 郑朝云,张式程,译.北京: 机械工业出版社,1994．
【2】RADAJ D. 焊接结构疲劳强度[M]. 郑朝云,张式程,译.北京: 机械工业出版社,1994．
相关信息