Analysis and Preventing of Hydrogen-induced Fracture of Auto Parts
摘 要
对氢脆的机理、氢脆的断口形貌、氢脆的表观形式、影响氢脆的因素、氢脆的预防以及氢脆的检查分别进行了介绍,并通过对汽车生产中典型氢致断裂案例的分析和研究,对氢脆断口形貌提出了判定依据: 脆性断口﹑沿晶断裂﹑显微气孔、二次裂纹、发线花纹。并依据氢脆发生的机理和主要影响因素,强调对于高强度零件及时有效地进行去氢处理的重要性。
Abstract
Mechanism, fracture morphologies, showing form, influence factors, preventive measures and testing method of hydrogen embrittlement were introduced. Some distinguishing bases for hydrogen-induced embrittlement fracture were put forward after analysis and research on the typical cases occurring in the auto parts processing. These bases included brittle fracture, intergranular fracture, micro-cavities, secondary cracks and hair thread pattern. The importance of timely and effective dehydrogenizing processing for high-strength parts was emphasized according to the formation mechanism and the affecting factors of hydrogen embrittlement.
中图分类号 U463.2
所属栏目 实践经验
基金项目
收稿日期 2009/4/24
修改稿日期
网络出版日期
作者单位点击查看
备注张 斌(1975-),男,助理工程师,学士。
引用该论文: ZHANG Bin,CHEN Xiao-gong,HU Si-jun. Analysis and Preventing of Hydrogen-induced Fracture of Auto Parts[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(4): 271~273
张 斌,陈小工,胡四军. 汽车零部件氢致断裂的分析及预防[J]. 理化检验-物理分册, 2010, 46(4): 271~273
被引情况:
【1】杨星红,梁 宇,王 卓, "10B21钢螺纹轴断裂失效分析",机械工程材料 40, 107-110(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】田永江. 金属的断裂失效分析[M]. 北京: 北京航空学院出版社,1982: 295-314.
【2】钟群鹏,赵子华. 断口学[M]. 北京: 高等教育出版社,2005: 212-220.
【3】陈南平,顾守仁,沈万慈. 机械零件失效分析[M]. 北京: 清华大学出版社,1988: 127-129.
【2】钟群鹏,赵子华. 断口学[M]. 北京: 高等教育出版社,2005: 212-220.
【3】陈南平,顾守仁,沈万慈. 机械零件失效分析[M]. 北京: 清华大学出版社,1988: 127-129.
相关信息