用电解抛光法制备大应变量SWRH82B钢丝EBSD试样
High Strain SWRH82B Steel Wire Sample Preparation for EBSD with Electrolytic Polishing
摘 要
提出了适合大应变量SWRH82B钢丝的电解抛光工艺参数。用电解抛光法制备该种材料的EBSD试样时,温度、电压和时间均对试样的菊池花样有重要影响。试样去应力退火后再进行电解抛光,可得到更好的花样质量。
SWRH82B 钢丝
EBSD
电解抛光
试样制备
菊池花样
high strain
SWRH82B steel wire
EBSD
electrolytic polishing
sample preparation
Kikuchi pattern
Abstract
Suitable parameters were introduced for electrolytic polishing method for high strain SWRH82B steel wire. When prepared electron backscatter diffraction (EBSD) samples with electrolytic polishing method, temperature, voltage and time impacted the quality of Kikuchi pattern. After relieving annealing, better Kikuchi pattern can be prepared with electrolytic polishing method.
中图分类号 TG115.21+1.2
所属栏目 试验技术与方法
基金项目
收稿日期 2010/1/14
修改稿日期
网络出版日期
作者单位点击查看
备注姚小燕(1985-),女,硕士研究生。
引用该论文: YAO Xiao-yan,LI Fan,WANG Lei. High Strain SWRH82B Steel Wire Sample Preparation for EBSD with Electrolytic Polishing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(5): 306～309
姚小燕,李 凡,王 雷. 用电解抛光法制备大应变量SWRH82B钢丝EBSD试样[J]. 理化检验－物理分册, 2010, 46(5): 306～309
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李华清,谢水生. 取向成像电子显微术试样的制备[J]. 理化检验-物理分册,2004,40(12):612-615．
【2】王雷. 冷拔高碳钢丝微观组织及织构演变规律[D]. 南京:东南大学,2009．
【3】张居生.不锈钢电解抛光工艺的研究与工业应用[J]. 腐蚀与防护, 2002,22(11): 498-502．
【4】张素银,杜凯,谌加军,等. 电解抛光技术研究进展[J]. 电镀与涂饰, 2007,26(2):48-53．
【5】毛卫民,杨平,陈冷. 材料织构分析原理与检测技术[M]. 北京: 冶金工业出版社,2005: 147．
【6】徐家文,云乃彰,王建业,等.电化学加工技术:原理、工艺及应用[M].北京:国防工业出版社,2008:96．
【7】张大同. 扫描电镜与能谱仪分析技术[M]. 广州: 华南理工大学出版社,2009:81．
【2】王雷. 冷拔高碳钢丝微观组织及织构演变规律[D]. 南京:东南大学,2009．
【3】张居生.不锈钢电解抛光工艺的研究与工业应用[J]. 腐蚀与防护, 2002,22(11): 498-502．
【4】张素银,杜凯,谌加军,等. 电解抛光技术研究进展[J]. 电镀与涂饰, 2007,26(2):48-53．
【5】毛卫民,杨平,陈冷. 材料织构分析原理与检测技术[M]. 北京: 冶金工业出版社,2005: 147．
【6】徐家文,云乃彰,王建业,等.电化学加工技术:原理、工艺及应用[M].北京:国防工业出版社,2008:96．
【7】张大同. 扫描电镜与能谱仪分析技术[M]. 广州: 华南理工大学出版社,2009:81．
相关信息