锅炉水冷却管爆裂原因分析
Bursting Reason Analysis for Water Cooling Tube of Boiler
摘 要
通过宏观检查、金相检验、化学成分及能谱分析等方法对锅炉水冷却管爆裂原因进行了分析。结果表明: 爆裂处管子局部受热,导致显微组织发生变化,使钢管金属材料的力学性能下降,受热面变形,管子慢慢胀粗导致管壁减薄,引起管子鼓包、穿孔直至开裂,造成爆管。
局部受热
爆裂
超温运行
water cooling tube of boiler
local heated
bursting
run at over-temperature
Abstract
By means of macro inspection, metallographic examination, chemical composition analysis and EDS analysis,the bursting reasons of the water cooling tube of boiler were analyzed. The results showed that the tube where was bursting had been local heating, the microstructure had changed, the mechanical properties of metal materials of the tube decreased, thermal deformation happened on the heating surface, causing the pipeline wall thinning, the bulge deformation and perforation, tube bursting.
中图分类号 TK229.5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/5/24
修改稿日期
网络出版日期
作者单位点击查看
备注陈现景(1982-),女,助理工程师，硕士。
引用该论文: CHEN Xian-jing,ZHANG Shou-peng,TANG Kong-ke,YANG Xiao-jie,TENG Yan,YANG Sen,SONG Jia-fang. Bursting Reason Analysis for Water Cooling Tube of Boiler[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(5): 337～339
陈现景,张守鹏,唐孔科,杨晓洁,滕 彦,杨 森,宋甲芳. 锅炉水冷却管爆裂原因分析[J]. 理化检验－物理分册, 2010, 46(5): 337～339
被引情况:
【1】刘广兴,犹公,张虔,龚巍,申雷, "锅炉冷灰斗水冷壁管泄漏原因分析",理化检验－物理分册 49, 119-122(2013)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黎家新,刘娜. 浅析DZL 20-13型锅炉水冷壁爆管[J]. 黑龙江科技信息,2008(31): 6．
【2】李炯辉. 金属材料金相图谱[M]. 北京: 机械工业出版社, 2006: 43-55．
【3】马庆谦,游菊. 锅炉水冷壁管爆管原因分析[J]. 理化检验-物理分册, 2004,40(9):465-468．
【4】机械工业理化检验人员技术培训和资格鉴定委员会. 金相检验[M].上海: 科学普及出版社, 2003:37-40．
【5】林介东,钟万里,盘荣旋. 燃煤锅炉水冷壁管爆管原因分析[J]. 理化检验-物理分册, 2005,41(4):203-204．
【6】史美堂. 金属材料及热处理[M]. 上海: 上海科学技术出版社, 1984．
【2】李炯辉. 金属材料金相图谱[M]. 北京: 机械工业出版社, 2006: 43-55．
【3】马庆谦,游菊. 锅炉水冷壁管爆管原因分析[J]. 理化检验-物理分册, 2004,40(9):465-468．
【4】机械工业理化检验人员技术培训和资格鉴定委员会. 金相检验[M].上海: 科学普及出版社, 2003:37-40．
【5】林介东,钟万里,盘荣旋. 燃煤锅炉水冷壁管爆管原因分析[J]. 理化检验-物理分册, 2005,41(4):203-204．
【6】史美堂. 金属材料及热处理[M]. 上海: 上海科学技术出版社, 1984．
相关信息