Fatigue Failure Reason of Rolling Bearing in Use
摘 要
为减少轴承疲劳失效现象的发生,提高其使用寿命,从原材料的质量、轴承的加工精度和滚动轴承的工作状况分析了滚动轴承疲劳失效产生的原因,包括原材料缺陷、热处理后的组织状态、工作表面加工质量、安装质量、使用状况以及润滑介质等,并提出了相应的改进措施。
Abstract
In order to reduce the occurrence of the fatigue failure phenomenon of rolling bearing and improve the life of rolling bearing, the fatigue failure reasons were analyzed from the raw material quality and processing precision and working conditions of the rolling bearings. The reasons included the defects in raw material, microstructure after heat treatment, processing quality of work surface, installation quality, using status and lubricating medium and so on. And the corresponding improvement measures were put forword.
中图分类号 TH133.33
所属栏目 实践经验
基金项目
收稿日期 2010/2/21
修改稿日期
网络出版日期
作者单位点击查看
备注陆琛元(1964-),男,工程师。
引用该论文: LU Chen-yuan,HU Chang-chun. Fatigue Failure Reason of Rolling Bearing in Use[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(5): 340~342
陆琛元,胡长春. 实际使用中滚动轴承发生疲劳失效的原因[J]. 理化检验-物理分册, 2010, 46(5): 340~342
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 24611-2009 滚动轴承 损伤和失效术语、特征及原因[S] .
【2】王广生. 金属热处理缺陷分析及案例[M]. 北京: 机械工业出版社,1997.
【3】尹延国. 滚动轴承疲劳失效过程的分析与研究[J]. 润滑与密封,1997(5):22-27.
【2】王广生. 金属热处理缺陷分析及案例[M]. 北京: 机械工业出版社,1997.
【3】尹延国. 滚动轴承疲劳失效过程的分析与研究[J]. 润滑与密封,1997(5):22-27.
相关信息