铁-铝金属间化合物涂层退火工艺的正交试验设计
Orthogonal Design of Annealing Technics for Fe-Al Intermetallic Compound Coating
摘 要
采用火焰喷涂-感应重熔工艺在45钢基体上制备铁-铝金属间化合物涂层，对其退火热处理工艺进行正交设计，得出优化的工艺为750 ℃退火1.5 h。优化退火后涂层的磨屑及磨损后试样表面形貌分析表明: 涂层的主要磨损机制开始为粘着磨损，随后转变为磨粒磨损。由扫描电子显微镜分析可知: 退火后铁-铝金属间化合物涂层由固溶体、条块状碳化物、氧化物和孔隙组成。
正交试验
退火
磨损机制
Fe-Al coating
orthogonal experiment
annealing
wear mechanism
Abstract
Fe-Al intermetallic compound coating was prepared on 45 steel substrate by flame spraying-induction remelting. The annealing technics was optimized by orthogonal experiment design, as annealing at 750 ℃ for 1.5 h. The wear mechanism of the coating, revealed by abrasive dust analysis and surface observation after wear, was the adhesive wear at the beginning followed by the abrasive particle wear. The microstructure of the annealed Fe-Al intermetallic compound coating was composed of solid solution, strip shaped and massive carbides, oxides and pores, as analyzed by SEM-EDS.
中图分类号 TG174.442
所属栏目 试验与研究
基金项目
收稿日期 2009/12/15
修改稿日期
网络出版日期
作者单位点击查看
备注荣鼎慧(1983-),女,硕士。
引用该论文: RONG Ding-hui,LIU Ying-cai,ZHOU Yong-jun,ZHANG Yu-ming,DING Li-li. Orthogonal Design of Annealing Technics for Fe-Al Intermetallic Compound Coating[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(7): 419～422
荣鼎慧,刘英才,周拥军,张玉明,丁莉莉. 铁-铝金属间化合物涂层退火工艺的正交试验设计[J]. 理化检验－物理分册, 2010, 46(7): 419～422
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李成功, 姚熹. 当代社会经济的先导——新材料[M]. 北京: 新华出版社, 1992:55-95．
【2】尹衍升, 施忠良, 刘俊友. 铁铝金属间化合物——合金化与成分设计[M]. 北京: 机械工业出版社, 1996:80-123．
【3】倪瑞澄, 孙震. 金属间化合物及其粉末冶金材料[J]. 粉末冶金技术, 1989, 7(4): 253-260．
【4】程广萍, 何宜柱. 激光熔覆制备Fe-Al复层的研究[J]. 焊接学报, 2006, 27(6): 37-39．
【5】李松瑞, 周善出. 金属热处理[M]. 长沙: 中南大学出版社, 2005:2-20．
【6】王灿明, 孙宏飞, 万殿茂. 高温扩散法制备铁铝金属间化合物涂层[J]. 材料保护, 2003, 36(3): 87-90．
【7】RODRGUEZ J, MARTN A, FERN/INDEZ R,et al. An experimental study of the wear performance of NiCrBSi thermal spray coatings[J]. Wear, 2003(255): 952-955．
【8】李静. Fe3Al基复合摩擦材料的制备与研究[D]. 济南: 山东大学, 2004．
【9】陈瑶, 王华明. 激光熔覆TiC增强FeAl金属间化合物基复合材料涂层磨损性研究[J]. 稀有金属材料与工程, 2003, 32(10): 842-846．
【10】吴树森, 严有为. 材料成形界面工程[M]. 北京: 化学工业出版社, 2006:124-126．
【11】KRATOVHVIL P, NEUMANN H. Welds of Fe3Al-type alloy with hardened structure[J]. Intermetallics, 2009(17): 378-380．
【12】GROSDIDIER T T,LIAO H L, TIDU A. X-rays and TEM characterization of nanocrystalline iron aluminide coatings prepared by HVOF thermal spraying[C]// Proceedings of 2000’NTSC.[s.l.]:[s.n],2000:1341-1344．
【2】尹衍升, 施忠良, 刘俊友. 铁铝金属间化合物——合金化与成分设计[M]. 北京: 机械工业出版社, 1996:80-123．
【3】倪瑞澄, 孙震. 金属间化合物及其粉末冶金材料[J]. 粉末冶金技术, 1989, 7(4): 253-260．
【4】程广萍, 何宜柱. 激光熔覆制备Fe-Al复层的研究[J]. 焊接学报, 2006, 27(6): 37-39．
【5】李松瑞, 周善出. 金属热处理[M]. 长沙: 中南大学出版社, 2005:2-20．
【6】王灿明, 孙宏飞, 万殿茂. 高温扩散法制备铁铝金属间化合物涂层[J]. 材料保护, 2003, 36(3): 87-90．
【7】RODRGUEZ J, MARTN A, FERN/INDEZ R,et al. An experimental study of the wear performance of NiCrBSi thermal spray coatings[J]. Wear, 2003(255): 952-955．
【8】李静. Fe3Al基复合摩擦材料的制备与研究[D]. 济南: 山东大学, 2004．
【9】陈瑶, 王华明. 激光熔覆TiC增强FeAl金属间化合物基复合材料涂层磨损性研究[J]. 稀有金属材料与工程, 2003, 32(10): 842-846．
【10】吴树森, 严有为. 材料成形界面工程[M]. 北京: 化学工业出版社, 2006:124-126．
【11】KRATOVHVIL P, NEUMANN H. Welds of Fe3Al-type alloy with hardened structure[J]. Intermetallics, 2009(17): 378-380．
【12】GROSDIDIER T T,LIAO H L, TIDU A. X-rays and TEM characterization of nanocrystalline iron aluminide coatings prepared by HVOF thermal spraying[C]// Proceedings of 2000’NTSC.[s.l.]:[s.n],2000:1341-1344．
相关信息