某电厂600 MW机组叶片断裂分析
Fracture Analysis of 600 MW Set Blade in Power Plant
摘 要
某电厂600 MW超超临界机组在检修中发现一只低压叶片断裂，采用宏观分析、金相检验以及断口分析等方法对叶片断裂原因进行了分析。结果表明: 叶片服役环境中存在能够引起叶片材料产生腐蚀的氯离子，导致叶片发生腐蚀疲劳断裂。
腐蚀介质
腐蚀疲劳
断裂
blade
corrosive medium
corrosion fatigue
fracture
Abstract
A low-pressure blade which used for the 600 MW super-hypercritic set of a power plant has fractured. The fracture reason was analyzed by means of macroscopic inspection, metallographic examination and fracture analysis. The results showed that the main reason caused blade fracture were that chlorine ions which can lead to corrosion existed in the working environment. And the fracture type of the blade was the corrosion fatigue fracture.
中图分类号 TK263.3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/10/27
修改稿日期
网络出版日期
作者单位点击查看
备注訾壮辉(1963-),男,高级工程师。
引用该论文: ZI Zhuang-hui,WANG Mei-ying. Fracture Analysis of 600 MW Set Blade in Power Plant[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(7): 459～461
訾壮辉,王梅英. 某电厂600 MW机组叶片断裂分析[J]. 理化检验－物理分册, 2010, 46(7): 459～461
被引情况:
【1】院冰,吴伟,田珂, "某伺服机构摩擦片断裂分析",理化检验－物理分册 47, 451-453(2011)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张承志. 金属的腐蚀与保护[M]. 北京: 冶金工业出版社，1987．
【2】刘永辉,张佩芬. 金属腐蚀学原理[M]. 北京: 航空工业出版社，1993．
【2】刘永辉,张佩芬. 金属腐蚀学原理[M]. 北京: 航空工业出版社，1993．
相关信息