1Cr18Ni9Ti不锈钢输油管道开裂原因分析
Cracking Reason Analysis of 1Cr18Ni9Ti Stainless Steel Oil Pipeline
摘 要
通过化学成分分析、宏观检验、金相检验和断口分析等方法对1Cr18Ni9Ti不锈钢液压油输送管道开裂原因进行了分析。结果表明：不锈钢管开裂为应力腐蚀开裂，裂纹起源于管道外壁并逐渐向内壁扩展；产生开裂的主要原因是工业水中氯、硫和氧等腐蚀性物质不断在钢管外壁沉积，在管道压力和腐蚀介质共同作用下，不锈钢管发生应力腐蚀开裂。
输油管道
腐蚀介质
应力腐蚀开裂
1Cr18Ni9Ti stainless steel
oil pipeline
corrosive medium
stress corrosion cracking
Abstract
The cracking reason of 1Cr18Ni9Ti stainless steel oil pipeline was investigated by means of chemical composition analysis, macroscopic inspection, metallographic examination and fracture analysis. The results showed that the cracking on stainless pipe belonged to stress corrosion cracking. Crack initiated from the outer surface of pipe and expanded to the inner surface of pipe. The cracking reason was that corrosive medium including elements of Cl,S and O in industrial water deposited on the outer surface of pipe. Because of the interaction of pipe pressure and corrosive medium, stress corrosion cracking occurred in stainless steel pipe.
中图分类号 TE973
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/10/27
修改稿日期
网络出版日期
作者单位点击查看
备注汪瑞俊(1983-),男,助理工程师。
引用该论文: WANG Rui-jun,WANG Yue,CHEN Lian-man. Cracking Reason Analysis of 1Cr18Ni9Ti Stainless Steel Oil Pipeline[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(9): 586～588
汪瑞俊,王越,陈联满. 1Cr18Ni9Ti不锈钢输油管道开裂原因分析[J]. 理化检验－物理分册, 2010, 46(9): 586～588
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李炯辉，林德成，陈金宝,等. 金属材料金相图谱[M]. 北京:机械工业出版社，2006．
【2】崔约贤,王长利. 金属断口分析[M]. 哈尔滨：哈尔滨工业大学出版社， 2006．
【3】王建军,郑文龙. 丙烯球罐底部排放阀连接螺栓断裂原因分析[J]. 腐蚀与防护,2003,24(11):500-503．
【4】顾宝珊,纪晓春,刘建华. 奥氏体不锈钢的应力腐蚀开裂[J].石油化工腐蚀与防护,2005,22(6): 41-44．
【2】崔约贤,王长利. 金属断口分析[M]. 哈尔滨：哈尔滨工业大学出版社， 2006．
【3】王建军,郑文龙. 丙烯球罐底部排放阀连接螺栓断裂原因分析[J]. 腐蚀与防护,2003,24(11):500-503．
【4】顾宝珊,纪晓春,刘建华. 奥氏体不锈钢的应力腐蚀开裂[J].石油化工腐蚀与防护,2005,22(6): 41-44．
相关信息