光学显微镜检测非金属夹杂物长度的不确定度评定
Uncertainty Evaluation on Measurement Results of Length of Non-metallic Inclusions
摘 要
根据JJF 1059-1999和GB/T 10561-2005, 采用光学显微镜及金相图像分析软件对某轧制比大于3的LZ50钢轴坯的非金属夹杂物长度进行了观察和测量, 按A法检验, 放大100倍观察, 对检测非金属夹杂物长度的测量不确定度来源进行了分析, 并对每个不确定度分量进行了评定, 最终给出了扩展不确定度及测量结果的不确度报告。结果表明: LZ50钢轴坯中的非金属夹杂物主要为C类细系硅酸盐夹杂物; 测量结果的不确定度报告为, 最严重视场C类非金属夹杂物总长度的测量值为(632±6) μm,k=2。
长度
不确定度评定
non-metallic inclusions
length
uncertainty evaluation
Abstract
According to the standard of JJF 1059-1999 and GB/T 10561-2005, the length of non-metallic inclusions in LZ50 steel shaft blank whose rolling proportion is more than 3 was observed by optical microscope and measured by metallographical analysis software in the multiple of 100 by method A of GB/T 10561-2005. The source of uncertainty in measuring the length of non-metallic inclusions was analyzed, every uncertainty component was evaluated, and finally the expanded uncertainty and measuring uncertainty report was offered. The results show that the main inclusions in LZ50 steel were type C silicate inclusions. The measuring uncertainty report was the measurement result of length of type C non-metallic inclusions was (632±6) μm, k=2.
中图分类号 TG142
所属栏目 试验技术与方法
基金项目
收稿日期 2010/1/13
修改稿日期
网络出版日期
作者单位点击查看
备注王立辉(1979-), 男, 工程师, 研究生。
引用该论文: WANG Li-hui. Uncertainty Evaluation on Measurement Results of Length of Non-metallic Inclusions[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(10): 637～640
王立辉. 光学显微镜检测非金属夹杂物长度的不确定度评定[J]. 理化检验－物理分册, 2010, 46(10): 637～640
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘智敏. 实验室认可中的不确定度和统计分析[M]. 北京: 中国标准出版社, 2007.
【2】宋余九, 荀毓闽．热处理质量控制和检验[M]//中国机械工程学会热处理学会. 热处理手册:4卷. 北京: 机械工业出版社, 2001.
【3】上海市机械制造工艺研究所． 金相分析技术[M]． 上海: 上海科学技术文献出版社, 1987.
【2】宋余九, 荀毓闽．热处理质量控制和检验[M]//中国机械工程学会热处理学会. 热处理手册:4卷. 北京: 机械工业出版社, 2001.
【3】上海市机械制造工艺研究所． 金相分析技术[M]． 上海: 上海科学技术文献出版社, 1987.
相关信息