金属材料布氏硬度试验的不确定度评定
Uncertainty Evaluation on Metallic Materials Brinell Hardness Test
摘 要
按照新的金属材料布氏硬度试验方法标准GB/T 231.1-2009对某硬度值为106 HBW10/1000的标准硬度块进行了布氏硬度测试, 并对布氏硬度测试结果的不确定度进行了评定; 同时还对新标准中关于测试结果不确定度评定的一些细节进行了说明, 对新标准中某些不确定度分量的评定方法提出了自己的观点。结果表明: 所测硬度块的布氏硬度测试结果为(107.2±5.0) HBW10/1000,k=2。
布氏硬度试验
评定方法
uncertainty evaluation
Brinell hardness test
evaluation method
Abstract
According to the new metallic materials Brinell hardness test standard GB/T 231.1-2009, the Brinell hardness test was done to a standard hardness block with hardness of 106 HBW10/1000, and the uncertainty for Brinell hardness test was evaluated. Some details of uncertainty evaluation for Brinell hardness test in new standard were illustrated. At the same time author’s opinions about the evaluation method of some uncertainty components in GB/T 231.1-2009 were proposed. The result show that the Brinell hardness value of the tested hardness block is (107.2±5.0) HBW10/1000, k=2.
中图分类号 TG113.25
所属栏目 标准化
基金项目
收稿日期 2010/4/25
修改稿日期
网络出版日期
作者单位点击查看
备注王 俊(1976-),男,工程师, 硕士。
引用该论文: WANG Jun,WANG Yu-ling. Uncertainty Evaluation on Metallic Materials Brinell Hardness Test[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(12): 771～774
王俊,王玉玲. 金属材料布氏硬度试验的不确定度评定[J]. 理化检验－物理分册, 2010, 46(12): 771～774
被引情况:
【1】王俊,王玉玲, "金属材料力学性能测试不确定度评定的探讨",理化检验－物理分册 50, 818-821(2014)
【2】杨震,王伟,吴广磊,徐婷婷,裴洪磊,范增, "提高铸铁材料布氏硬度快速测试精度的方法",理化检验－物理分册 51, 772-775(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】国合格评定国家认可委员会. CNAS-GL10: 2006《材料理化检验测量不确定度评估指南及实例》（王承忠 主编）[M]. 北京: 中国计量出版社, 2007.
【2】刘全红. 金属布氏硬度计示值误差不确定度分析与评定[J]. 现代测量与实验室管理, 2001(1): 35-47.
【3】马纪衡, 高生龙. 布氏硬度试验中测量的不确定度评定[J]. 甘肃冶金, 2005, 27（1）: 26-28.
【4】JJF 1059-1999测量不确定度评定与表示[S].
【5】倪育材. 实用测量不确定度评定[M]. 北京: 中国计量出版社, 2009.
【2】刘全红. 金属布氏硬度计示值误差不确定度分析与评定[J]. 现代测量与实验室管理, 2001(1): 35-47.
【3】马纪衡, 高生龙. 布氏硬度试验中测量的不确定度评定[J]. 甘肃冶金, 2005, 27（1）: 26-28.
【4】JJF 1059-1999测量不确定度评定与表示[S].
【5】倪育材. 实用测量不确定度评定[M]. 北京: 中国计量出版社, 2009.
相关信息