满滚子轴承滚柱脱落与掉块原因分析
Sunface Exfoliation and Flaking Reason Analysis on Rollers of Full Ball Bearing
摘 要
某厂生产的满滚子轴承仅使用5 d, 其滚柱表面就发生了脱落与掉块失效。采用宏观分析、金相检验、化学成分分析和硬度检测等方法对滚柱表面脱落与掉块的原因进行了分析。结果表明: 滚柱回火不充分、表面渗碳层硬度梯度变化较大、心部显微组织不均匀以及心部硬度偏低是导致滚柱表面脱落与掉块的主要原因。
脱落与掉块
回火
硬度
显微组织
roller
exfoliation and flaking
tempering
hardness
microstructure
Abstract
Rollers of the full ball bearing which only being used for 5 days failed with surface exfoliation and flaking. By adopting macro examination, metallographic examination,chemical compositions analysis and hardness test the failure reason was analyzed. The result indicate that not sufficient tempering, steep carburized layer hardness gradient, nouniform centre microstructure and lower centre hardness were all main reasons that resulted in the surface exfoliation and flaking of the rollers.
中图分类号 TH133.33+2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2010/3/28
修改稿日期
网络出版日期
作者单位点击查看
备注王培科(1983-),男, 工程师, 学士。
引用该论文: WANG Pei-ke,WANG Wei-fa. Sunface Exfoliation and Flaking Reason Analysis on Rollers of Full Ball Bearing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(12): 791～793
王培科,王维发. 满滚子轴承滚柱脱落与掉块原因分析[J]. 理化检验－物理分册, 2010, 46(12): 791～793
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】蔡宏伟. 金相检验[M]. 上海: 上海科学普及出版社, 2003.
【2】黄振东. 钢铁金相图谱[M]. 北京: 中国科技文化出版社, 2005.
【3】夏立芳. 金属热处理工艺学[M]. 哈尔滨: 哈尔滨工业大学出版社, 2004.
【4】孙智, 江利, 应鹏展. 失效分析基础与应用[M]. 北京: 机械工业出版社, 2007.
【5】中国机械工程学会热处理学会. 热处理手册[M]. 北京: 机械工业出版社, 2008.
【6】张栋. 机械失效的实用分析[M]. 北京: 国防工业出版社, 1997.
【2】黄振东. 钢铁金相图谱[M]. 北京: 中国科技文化出版社, 2005.
【3】夏立芳. 金属热处理工艺学[M]. 哈尔滨: 哈尔滨工业大学出版社, 2004.
【4】孙智, 江利, 应鹏展. 失效分析基础与应用[M]. 北京: 机械工业出版社, 2007.
【5】中国机械工程学会热处理学会. 热处理手册[M]. 北京: 机械工业出版社, 2008.
【6】张栋. 机械失效的实用分析[M]. 北京: 国防工业出版社, 1997.
相关信息