DN2-6井套管压力升高及油管接头粘扣原因分析
Cause Analysis on Casing Pressure Increasing and Tubing Connections Galling in Well DN2-6
摘 要
对DN2-6井套管压力升高原因进行了系统调查研究,对起出的油管接头逐根进行检查, 发现1根油管穿孔、多根油管粘扣, 并对油管粘扣原因也进行了分析。结果表明: 套管压力升高的原因主要是由油管穿孔所致; 油管粘扣的原因主要是由对扣操作不当所致; 粘扣会降低油管接头的密封能力, 但该井粘扣的油管接头并没有发生泄漏, 其原因是在油管穿孔泄漏之后, 油管柱所受的内压很小, 没有达到粘扣油管接头的泄漏抗力。
套管压力
泄漏
粘扣
穿孔
tubing connection
casing pressure
leakage
galling
piercing
Abstract
The cause of casing pressure increasing in well DN2-6 was investigated and tubings taken out from this well were inspected one by one. It was found that there were one tubing pierced and many tubings connections galled, and the galling reason was also analyzed. The results show that the tubing perforation resulted in the casing pressure increasing, and tubing connection gallings were caused due to abnormal operation. Galling would reduce the tubing connection seal capability, but the galling tubing connections did not leak because the internal pressure borne by the tubing string was smaller than that of its seal capability after tubing perforation leaking.
中图分类号 TE931+.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2010/3/7
修改稿日期
网络出版日期
作者单位点击查看
备注滕学清(1965-),男,高级工程师。
引用该论文: TENG Xue-qing,LV Shuan-lu,HUANG Shi-cai,LI Yuan-bin,WANG Zhen-biao,ZHOU Li-zhi,SHENG Shu-bin,LIU Ming-qiu,PENG Jian-yun,LI Jiang. Cause Analysis on Casing Pressure Increasing and Tubing Connections Galling in Well DN2-6[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(12): 794～797
滕学清,吕拴录,2,黄世财,李元斌,王振彪,周理志,盛树彬,刘明球,彭建云,李江. DN2-6井套管压力升高及油管接头粘扣原因分析[J]. 理化检验－物理分册, 2010, 46(12): 794～797
被引情况:
【1】滕学清,吕拴录,李宁,秦宏德,丁毅,刘德英,杜涛,徐永康, "φ177.8 mm偏梯形螺纹套管粘扣原因分析",理化检验－物理分册 50, 780-784(2014)
【2】杨向同,吕拴录,彭建新,王鹏,宋文文,李金凤,耿海龙,文志明,徐永康,石桂军, "某油井特殊螺纹接头油管粘扣原因分析",理化检验－物理分册 52, 320-323(2016)
【3】安文华,滕学清,吕拴录,张新平,杨成新,丁毅,杜涛,徐永康, "塔里木油田非API油套管技术要求及标准化",理化检验－物理分册 49, 103-106(2013)
【4】张钧,赵国仙,吕祥鸿,宋文文, "塔里木油田某井油管脱落原因分析",理化检验－物理分册 50, 845-848(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吕拴录. 特殊螺纹接头油套管选用注意事项[J]. 石油技术监督2005,21（11）:12-14.
【2】吕拴录, 韩勇. 特殊螺纹接头油,套管使用及展望[J]. 石油工业技术监督,2003(3):1-4.
【3】API RECOMMENDED PRACTICE 90Annular Casing Pressure Management for Offshore Wells[S].
【4】吕拴录, 骆发前, 陈飞, 等. 牙哈7X-1井套管压力升高原因分析[J]. 钻采工艺, 2008, 31（1）: 129-132.
【5】张福祥,吕拴录,王振彪, 等. 某高压气井套管压力升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J]. 中国特种设备安全, 2010,26（5）: 65-68.
【6】吕拴录,常泽亮,吴富强,等. N80 LCSG套管上、卸扣试验研究[J]. 理化检验-物理分册, 2006,42(12): 602-605.
【7】吕拴录, 刘明球, 王庭建, 等. J55 平式油管粘扣原因分析[J]. 机械工程材料, 2006,30(3): 69-71.
【8】袁鹏斌, 吕拴录, 姜涛,等. 进口油管脱扣和粘扣原因分析[J]. 石油矿场机械, 2008, 37（3）: 74-77.
【9】吕拴录, 康延军, 孙德库, 等. 偏梯形螺纹套管紧密距检验粘扣原因分析及上卸扣试验研究[J]. 石油矿场机械, 2008, 37（10）: 82-85.
【10】L Shuan-lu,KANG Yan-jun,SUN De-ku,et al. Cause analysis and make up test investigation on casing galling during inspection[J]. Oil Field Equipment, 2008, 37（10）: 82-85.
【11】吕拴录,骆发前,赵盈, 等. 防硫油管粘扣原因分析及试验研究[J]. 石油矿场机械, 2009(8): 37-40.
【2】吕拴录, 韩勇. 特殊螺纹接头油,套管使用及展望[J]. 石油工业技术监督,2003(3):1-4.
【3】API RECOMMENDED PRACTICE 90Annular Casing Pressure Management for Offshore Wells[S].
【4】吕拴录, 骆发前, 陈飞, 等. 牙哈7X-1井套管压力升高原因分析[J]. 钻采工艺, 2008, 31（1）: 129-132.
【5】张福祥,吕拴录,王振彪, 等. 某高压气井套管压力升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J]. 中国特种设备安全, 2010,26（5）: 65-68.
【6】吕拴录,常泽亮,吴富强,等. N80 LCSG套管上、卸扣试验研究[J]. 理化检验-物理分册, 2006,42(12): 602-605.
【7】吕拴录, 刘明球, 王庭建, 等. J55 平式油管粘扣原因分析[J]. 机械工程材料, 2006,30(3): 69-71.
【8】袁鹏斌, 吕拴录, 姜涛,等. 进口油管脱扣和粘扣原因分析[J]. 石油矿场机械, 2008, 37（3）: 74-77.
【9】吕拴录, 康延军, 孙德库, 等. 偏梯形螺纹套管紧密距检验粘扣原因分析及上卸扣试验研究[J]. 石油矿场机械, 2008, 37（10）: 82-85.
【10】L Shuan-lu,KANG Yan-jun,SUN De-ku,et al. Cause analysis and make up test investigation on casing galling during inspection[J]. Oil Field Equipment, 2008, 37（10）: 82-85.
【11】吕拴录,骆发前,赵盈, 等. 防硫油管粘扣原因分析及试验研究[J]. 石油矿场机械, 2009(8): 37-40.
相关信息