电阻焊直缝焊接套管残余应力分布的测定
Determination of Residual Stress Distribution in ERW Casing
摘 要
采用X射线法结合环劈法对电阻焊直缝焊接套管的管体和焊缝的应力分布,以及焊接套管切割后应力的变化进行研究。结果表明：焊接套管残余应力在周向上分布不均,并且焊缝处残余应力很高,接近其屈服强度;焊接套管切割后管体外表面残余应力随着时效时间的增长由拉应力转为压应力,而内表面由压应力转为拉应力。
直缝焊接套管
残余应力
X射线衍射法
环劈法
ERW
straight welded casing
residual stress
X-ray diffraction method
cutting method
Abstract
The residual stress distribution of the ERW straight welded casing was studied by using X-ray diffraction and cutting methods. It had been found that the residual stress distribution exhibited a asymmetric characteristic along the circumferential direction,and the residual stress near the welding line was very high,close to the yield strength;The residual stress of exterior surface after cutting changed from tensile stress to compressive stress with the increase of aging time,while a reverse phenomenon was observed in the interior surface.
中图分类号 TG142
所属栏目 试验与研究
基金项目
收稿日期 2007/12/19
修改稿日期
网络出版日期
作者单位点击查看
备注董晓明(1980-),男,工程师。
引用该论文: DONG Xiao-ming,TIAN Qing-chao. Determination of Residual Stress Distribution in ERW Casing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 5～8
董晓明,田青超. 电阻焊直缝焊接套管残余应力分布的测定[J]. 理化检验－物理分册, 2009, 45(1): 5～8
被引情况:
【1】吕春雷,曹为民,陈浩,印仁和,董晓明,田青超, "应力对直缝高频电阻焊管沟槽腐蚀的影响",腐蚀与防护 31, 512-514(2010)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】辛希贤.管线钢的焊接[M].西安: 陕西科学技术出版社,1997:134．
【2】孙占刚,韩志凌.焊管成型过程研究综述[J]. 承德民族职业技术学院学报,2004(1):87．
【3】唐立峰,王立君,杨春阁. 大口径直缝焊管扩径后表面周向残余应力的估算[J]. 焊管,2006,29(2):13．
【4】朱维斗,李 年. 三种残余应力测试方法在石油输送管中的应用[J]. 焊管,1997,20(4):6．
【5】徐学利,辛希贤. ERW直缝套管残余应力分布规律的研究[J].石油机械,2003,31(3):1．
【2】孙占刚,韩志凌.焊管成型过程研究综述[J]. 承德民族职业技术学院学报,2004(1):87．
【3】唐立峰,王立君,杨春阁. 大口径直缝焊管扩径后表面周向残余应力的估算[J]. 焊管,2006,29(2):13．
【4】朱维斗,李 年. 三种残余应力测试方法在石油输送管中的应用[J]. 焊管,1997,20(4):6．
【5】徐学利,辛希贤. ERW直缝套管残余应力分布规律的研究[J].石油机械,2003,31(3):1．
相关信息