某型发动机加力点火喷嘴管断裂分析
Fracture Analysis of Igniter Nozzle Tube of Aeroengine Afterburner
摘 要
采用断口分析、X射线能谱分析、痕迹分析及金相检验等试验方法对断裂的发动机加力点火喷嘴管进行了综合分析。结果表明:装配应力大导致喷嘴管产生疲劳裂纹，疲劳裂纹起始于喷嘴管与加力内圈总管管座连接处的焊接根部,喷嘴管断裂性质为起始应力较大的高周疲劳断裂;在发动机大修重新装配喷嘴管时存在漏检问题。
疲劳
装配应力
nozzle tube
fatigue
assembly stress
Abstract
In order to analyze the reason for fracture of afterburner igniter nozzle tube,the means,such as characters of fracture,X-ray energy analysis,trace analysis and microstructure examination,were conducted. The results showed that the afterburner igniter nozzle tube failed due to high cycle fatigue fracture with high original stress,and fatigue crack started from welding zone between afterburner igniter nozzle tube and afterburner fuel manifold. The main cause of fatigue origination was excessive assembly stress which was created in the course of heavy repair assembly,and the issue of missed check also existed.
中图分类号 V215.5+5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/6/9
修改稿日期
网络出版日期
作者单位点击查看
备注吕凤军(1979-),男,工程师。
引用该论文: LV Feng-jun,FU Guo-ru,CHEN Rong. Fracture Analysis of Igniter Nozzle Tube of Aeroengine Afterburner[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 31～33
吕凤军,傅国如,陈荣. 某型发动机加力点火喷嘴管断裂分析[J]. 理化检验－物理分册, 2009, 45(1): 31～33
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】傅国如,张 峥.失效分析技术[J].理化分册-物理分册,2005,41(4):212-216．
【2】傅国如,张 峥.失效分析技术(续)[J].理化分册-物理分册,2005,41(6):318-323．
【3】张 峥.失效分析思路[J].理化检验-物理分册,2005,41(3):158-161．
【4】李 权,傅国如,徐志刚,等.航空发动机不锈钢导管失效分析[J].材料工程,2003(增刊):137-138．
【5】傅国如,陈 荣,吕凤军,等.发动机燃油导管断裂失效分析[J].失效分析与预防,2007(2):29-33．
【6】张 栋.机械失效的痕迹分析[M].北京:国防工业出版社,1996．
【2】傅国如,张 峥.失效分析技术(续)[J].理化分册-物理分册,2005,41(6):318-323．
【3】张 峥.失效分析思路[J].理化检验-物理分册,2005,41(3):158-161．
【4】李 权,傅国如,徐志刚,等.航空发动机不锈钢导管失效分析[J].材料工程,2003(增刊):137-138．
【5】傅国如,陈 荣,吕凤军,等.发动机燃油导管断裂失效分析[J].失效分析与预防,2007(2):29-33．
【6】张 栋.机械失效的痕迹分析[M].北京:国防工业出版社,1996．
相关信息