电站锅炉爆管事故原因分析
Reason Analysis of Boiler Tube Burst Accident in Power Station
摘 要
采用宏观检验、光谱分析、显微组织检验、硬度测定和室温抗拉强度测定等方法对一起电站锅炉爆管事故的原因进行了综合分析。结果表明:水冷壁管短时过热造成材料高温强度降低,从而引起爆管。
水冷壁管
爆裂
短时过热
boiler
water wall tube
burst
overheat in short time
Abstract
The reasons of boiler tube burst accident happened in one power station were analyzed by means of macro structure inspection,spectrum analysis,metallograph examination,hardness measuring,tensile strength testing in room temperature etc. The results showed that the boiler water wall tubes were overheated in short time,which led to the strength of tube reduced under high pressure environment,at last the boiler tube bursted.
中图分类号 TK223.3+1
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/10/9
修改稿日期
网络出版日期
作者单位点击查看
备注王建祥(1968-),男,高级工程师。
引用该论文: WANG Jian-xiang,YOU Xin-min,YUE Jian-xin,WANG Da-gang,LIANG Chang-ping,SONG Li-xia,XU Shu-de,CHEN Fu-zhi. Reason Analysis of Boiler Tube Burst Accident in Power Station[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 34～36
王建祥,游新民,岳建新,王大刚,梁长平,宋丽霞,徐树德,陈福枝. 电站锅炉爆管事故原因分析[J]. 理化检验－物理分册, 2009, 45(1): 34～36
被引情况:
【1】董登超,张珂,洪慧敏,顾锋, "某电厂锅炉用12Cr1MoVG钢过热器管爆管的原因",机械工程材料 40, 114-118(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】上海市机械制造工艺研究所.金相分析技术[M].上海：科学技术文献出版社,1987．
【2】GB 6397-1986金属拉伸试样[S]．
【3】上海市金属学会.金属材料缺陷金相图谱[M].上海：上海科学技术出版社,1996：40-49．
【4】韩德伟,张建新.金相试样制备与显示技术[M].广州：中山大学出版社,2005：33．
【5】屠世润,高 越.金相原理与实践[M].北京：机械工业出版社,1990：60,316．
【2】GB 6397-1986金属拉伸试样[S]．
【3】上海市金属学会.金属材料缺陷金相图谱[M].上海：上海科学技术出版社,1996：40-49．
【4】韩德伟,张建新.金相试样制备与显示技术[M].广州：中山大学出版社,2005：33．
【5】屠世润,高 越.金相原理与实践[M].北京：机械工业出版社,1990：60,316．
相关信息