齿面弧形裂纹分析
Analysis of Arc Crack on Gear Surface
摘 要
通过化学成分分析、硬度试验、宏观和微观检验等方法,对减速机齿轮齿面弧形裂纹的产生原因进行了分析。结果表明:该裂纹属于磨削裂纹,磨削工艺不当是裂纹产生的直接原因。热处理工艺不当也增加了齿轮磨裂的可能性。因此,在磨削工艺及热处理工艺方面提出了改进措施。
弧形裂纹
渗碳淬火
磨削
gear
arc crack
cementite quenching
mill
Abstract
The reason of arc crack on retarder gear surface was analyzed by means of chemical composition analysis,hardness testing,macrostructure and microstructure examination. The results showed that the mill cracks were produced by improper technology. And the probability of gear cracking was increased by heat treatment misoperation. So the improvement measures on the technology were put forward.
中图分类号 TH132.41
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/10/31
修改稿日期
网络出版日期
作者单位点击查看
备注冯文改(1972-),女,工程师。
引用该论文: FENG Wen-gai,XU Hai-jian. Analysis of Arc Crack on Gear Surface[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 37～38
冯文改,许海健. 齿面弧形裂纹分析[J]. 理化检验－物理分册, 2009, 45(1): 37～38
被引情况:
【1】苏虹,崔怀玲,戴维弟, "20CrNi2Mo钢齿轮磨削裂纹成因分析",理化检验－物理分册 50, 911-913(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】桂立丰. 轴承钢磨削变质层的研究[J].机械工程学报,1984,20(1)：39．
【2】夏立芳. 金属热处理工艺学[M].哈尔滨：哈尔滨工业大学出版社,1986：54．
【3】孙玉盛. 戴雅康.热处理裂纹分析图谱[M].大连：大连出版社,2002：102．
【2】夏立芳. 金属热处理工艺学[M].哈尔滨：哈尔滨工业大学出版社,1986：54．
【3】孙玉盛. 戴雅康.热处理裂纹分析图谱[M].大连：大连出版社,2002：102．
相关信息