烟气轮机叶片断裂原因分析
Rupture Reason Analysis of Gas Expander Blade
摘 要
采用化学成分分析、性能试验和金相检验等方法对运行中断裂的叶片进行了分析。结果表明:长期的超温运行使得该叶片晶粒长大,组织性能发生变化,导致叶片断裂事故的发生。
叶片
断裂
超温
晶粒
gas expander
blade
rupture
extraordinarily high temperature
grain
Abstract
The ruptured blade which had been used for a long time in the gas expander had been analyzed by means of chemical composition analysis,performance test and metallographic experiment. The results showed that,the reason which led to the rupture of blade was the grain growth of the blade material after a long time working under extraordinarily high temperature,and the changing of the microstructures and properties of the blade.
中图分类号 TQ052,TK263.3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/10/18
修改稿日期
网络出版日期
作者单位点击查看
备注章文兰(1958-),女,工程师。
引用该论文: ZHANG Wen-lan,DING Li-sheng,ZHANG Yu-feng. Rupture Reason Analysis of Gas Expander Blade[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 48～52
章文兰,丁利生,张玉峰. 烟气轮机叶片断裂原因分析[J]. 理化检验－物理分册, 2009, 45(1): 48～52
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Q/LJJ 0302-1998烟气轮机用864合金热轧棒料技术条件[S]．
【2】HG/T 3650-1999烟气轮机技术条件[S]．
【3】董建新,丁利生,王振德．轮盘和动叶片用Waspaloy合金研究[J]. 中国材料科技与设备,2006(2): 68-73．
【4】王茂才,刘湘生,王烈炯. 烟机涡轮盘和动叶片的损伤分析与激光随形熔铸重建[J]. 金属热处理,2002,27(10):17-21．
【5】董建新.实际服役烟机动叶片质量分析[D].北京:北京科技大学,2005．
【2】HG/T 3650-1999烟气轮机技术条件[S]．
【3】董建新,丁利生,王振德．轮盘和动叶片用Waspaloy合金研究[J]. 中国材料科技与设备,2006(2): 68-73．
【4】王茂才,刘湘生,王烈炯. 烟机涡轮盘和动叶片的损伤分析与激光随形熔铸重建[J]. 金属热处理,2002,27(10):17-21．
【5】董建新.实际服役烟机动叶片质量分析[D].北京:北京科技大学,2005．
相关信息