20MnSiNb热轧带肋钢筋屈服点不明显原因分析

Reason Analysis of No-yield-point of 20MnSiNb Hot Rolled Ribbed Bar

李海滨

张贺宗

高雷雷

摘要

对屈服点不明显的20MnSiNb热轧带肋钢筋进行了断口观察、化学成分测定及显微组织分析，并与力学性能正常的钢筋进行了对比。研究表明，贝氏体含量偏高是造成钢筋屈服不明显的主要原因。并提出了改进措施。

标签 20MnSiNb钢

热轧带肋钢筋

屈服点

20MnSiNb steel

hot rolled ribbed bar

yield point

Abstract

In order to find out the reason of no-yield-point of 20MnSiNb hot rolled ribbed bar,the fracture observation,chemical composition and microstructure were analyzed,and the comparison and analysis of normal mechanical properties were made as well. The results showed that the reason was the high content of bainite,and the measures were proposed.

中图分类号 TG142.41

所属栏目实践经验

基金项目

收稿日期 2007/11/21

修改稿日期

网络出版日期

作者单位点击查看

备注李海滨(1980-),男,助理工程师。

引用该论文: LI Hai-bin,ZHANG He-zong,GAO Lei-lei. Reason Analysis of No-yield-point of 20MnSiNb Hot Rolled Ribbed Bar[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 67～69
李海滨,张贺宗,高雷雷. 20MnSiNb热轧带肋钢筋屈服点不明显原因分析[J]. 理化检验－物理分册, 2009, 45(1): 67～69

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】崔忠圻. 金属学与热处理[M].北京:机械工业出版社,2000:178-183．

【2】马立明,王勇. 热轧带肋钢筋屈服点不明显的成因分析[J]. 河北冶金,2007(1): 57-58．

相关信息

	标题	相关频次
	45优质圆钢镦裂分析	4
	提高Q420角钢力学性能的探讨	4
	关于GB/T 1499.2-2018中热轧带肋钢筋截面维氏硬度检验方法的探讨	2
	混凝土结构用低合金钢筋的性能要求	2
	螺纹钢屈服强度与钢中元素的回归分析及应用	2
	螺纹摩擦对螺栓轴向力-伸长量特征曲线的影响	2
	犃犎32船板钢拉伸断口开裂原因分析	2
	热轧带肋钢筋拉伸试验结果的不确定度评定	2
	依据GB/T1499.2—2018标准的最大力总延伸率验证试验	2
	HRB400热轧带肋钢筋冷弯断裂原因分析	1
	HRB400热轧带肋钢筋弯曲加工断裂原因分析	1
	铝合金腐蚀声发射信号特性研究	1
	热轧带肋钢筋不同时间段力学性能的变化	1
	热轧带肋钢筋的全自动检测技术	1