Failure Analysis and Countermeasure About Roller for Hot Rolling Mill
摘 要
Cr-Ni-Mo无限冷硬Ⅳ材料轧辊在使用中出现了工作层剥落和炸裂的现象,经现场取样分析,并在实验室进行了系列温度的时效工艺试验和耐磨性试验的基础上确定了该材料热处理条件与性能之间的关系。无限冷硬Ⅳ材料轧辊经过(425±5)℃去应力处理后,可以得到最佳性能配合和使用效果。使轧制带钢的宽度增加了10%以上,即解决了生产中的轧辊质量问题,又为用户增加产品规格提供了条件,具有推广价值。
Abstract
In the field usage,there are many inactivation problem on the Cr-Ni-Mo chilled iron Ⅳ roller. By the sampling and analysis in the field,based on the laboratory experiments which included the series temperatures aging tests and the abradability tests,finally,established the relation on the heat-treatment condition and the property. By the stress relieving under the heat-treatment of the temperature,(425±5)℃,the Cr-Ni-Mo chilled iron Ⅳ composite roller can obtain the optimal property adaption and usage effect. That makes the width of rolling strip steels increased by more than 10%,then solve the quality problems of roller in the practice production and provide the conditions to increase product specifications for the user,affirmed by the user.
中图分类号 TG333.17
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/11/12
修改稿日期
网络出版日期
作者单位点击查看
备注那顺桑(1949-),男,教授。
引用该论文: NA Shun-sang,ZHANG Zi-li,GONG Kai-ling,GAO chun-li,HU Bing. Failure Analysis and Countermeasure About Roller for Hot Rolling Mill[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(2): 108~110
那顺桑,张自立,宫开令,高春利,胡冰. 热轧机轧辊失效分析及对策[J]. 理化检验-物理分册, 2009, 45(2): 108~110
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
相关信息