20Cr钢与B级钢焊接接头的组织和性能
Microstructures and Mechanical Properties of the Welded Joints of 20Cr Steel and Level-B Steel
摘 要
采用低温冲击试验、拉伸试验、硬度试验以及金相分析等方法对ER50-6焊丝气体保护焊焊接20Cr钢与B级钢焊接接头的显微组织和性能进行了研究。结果表明,用ER50-6焊丝气体保护焊焊接20Cr钢和B级钢可获得性能良好的焊接接头,其接头的强度不低于B级钢。焊缝组织为网状分布的先共析铁素体及少量无碳贝氏体; 20Cr钢侧近缝区有无碳贝氏体及少量板条马氏体;在B级钢侧热影响区的块状铁素体基体上有少量粒状贝氏体。
组织
力学性能
dissimilar steels welding
microstructure
mechanical property
Abstract
Microstructures and properties of 20Cr steel and level-B steel joints welded by gas metal arc welding with ER50-6 wire are investigated with low-temperature impact,room-temperature tensile test,hardness test and metallographic analysis. The results show that the joints welded by gas metal arc welding with ER50-6 wire have better performance and more strength than parent metal. The microstructure of welded metal mainly contains reticular proeutectoid ferrite and a little carbon-free bainite. Carbon-free bainite also appears in the HAZ of 20Cr steel together with little lath martensite ,while in the HAZ of level-B steel ,little granular bainite distributes on the blocky ferrite.
中图分类号 TG113
所属栏目 试验与研究
基金项目
收稿日期 2008/2/25
修改稿日期
网络出版日期
作者单位点击查看
备注许鸿吉(1959-),男,教授,工学博士。
引用该论文: XU Hong-ji,SONG Bing-xin,CHANG Li,JIN Guang,LI Hua,SU Qin. Microstructures and Mechanical Properties of the Welded Joints of 20Cr Steel and Level-B Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(3): 138～141
许鸿吉,宋冰昕,常 力,金 光,李 华,苏 琴. 20Cr钢与B级钢焊接接头的组织和性能[J]. 理化检验－物理分册, 2009, 45(3): 138～141
被引情况:
【1】尹丽香,魏志宇,宋冰昕, "淬火态20Cr钢与B级铸钢焊接接头冷热裂纹敏感性分析",理化检验－物理分册 50, 480-482(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】董 雯 赵 宜.热处理工艺对B级钢金相组织及力学性能的影响[J].机车车辆工艺,2001,10(5):10-12．
【2】中国机械工程学会焊接学会编.焊接手册(焊接材料) [M].北京: 机械工业出版社,1992．
【3】王成文.焊接材料手册及工程应用实例[M].太原：山西科学技术出版社,2004．
【4】崔忠折.金属学与热处理[M].北京：机械工业出版社,2001．
【2】中国机械工程学会焊接学会编.焊接手册(焊接材料) [M].北京: 机械工业出版社,1992．
【3】王成文.焊接材料手册及工程应用实例[M].太原：山西科学技术出版社,2004．
【4】崔忠折.金属学与热处理[M].北京：机械工业出版社,2001．
相关信息