铝合金锻件缺陷原因分析
Defect Reason Analysis of Aluminium Alloy Forgings
摘 要
某铝合金锻件在进行质量检查时发现了面状缺陷。采用显微组织检查、力学性能测试、化学成分分析、SEM和EDAX以及相控阵超声检测等方法对锻件缺陷产生的原因进行了分析。结果表明：锻件的缺陷是其在切割过程中产生的,其主要原因是锻件内部存在残余应力。
残余应力
开裂
相控阵超声
失效分析
aluminium alloy
residual stress
cracking
phased-array ultrasonic
failure analysis
Abstract
The defect in aluminum alloy forgings was found during the processing in quality inspection. Examinations and analysis were performed by means of microstructure inspection,mechanical property measurement,chemical composition analysis,SEM,EDAX,phased array ultrasonic inspection and so on. The results showed that the defect in forgings was produced during cutting. Residual stress was the main reason of cracking.
中图分类号 TG146.2+1
所属栏目 质量控制与失效分析
基金项目
收稿日期
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: XU Heng-ting,WU Long-fei,YUAN Yong. Defect Reason Analysis of Aluminium Alloy Forgings[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(3): 168～171
许恒庭,吴龙飞,袁 勇. 铝合金锻件缺陷原因分析[J]. 理化检验－物理分册, 2009, 45(3): 168～171
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】金相图谱编写组.变形铝合金金相图谱[M]. 北京:冶金工业出版社,1975:22,136．
【2】米谷.残余应力的产生和对策[M].朱荆璞,邵合孟,译.北京：机械工业出版社,1983．
【3】中国机械工程学会热处理专业委员会《热处理手册》编委会.热处理手册（第4卷：热处理质量控制检验方法）[M].北京：机械工业出版社,1992:185-194．
【4】陈明鸣,王元良.热处理工艺对LD10铝合金残余应力的影响[J]. 西南交通大学学报,1997,4 (2):198-202．
【5】王秋成,柯映林. 航空高强度铝合金残余应力的抑制与消除[J]. 航空材料学报,2002 (3):59-62．
【6】曾苏民.降低超厚铝合金锻件残余应力的试验[J]. 中国有色金属学报,1996,9 (3):67-70．
【2】米谷.残余应力的产生和对策[M].朱荆璞,邵合孟,译.北京：机械工业出版社,1983．
【3】中国机械工程学会热处理专业委员会《热处理手册》编委会.热处理手册（第4卷：热处理质量控制检验方法）[M].北京：机械工业出版社,1992:185-194．
【4】陈明鸣,王元良.热处理工艺对LD10铝合金残余应力的影响[J]. 西南交通大学学报,1997,4 (2):198-202．
【5】王秋成,柯映林. 航空高强度铝合金残余应力的抑制与消除[J]. 航空材料学报,2002 (3):59-62．
【6】曾苏民.降低超厚铝合金锻件残余应力的试验[J]. 中国有色金属学报,1996,9 (3):67-70．
相关信息