TP2铜螺旋管裂纹产生原因分析
Crack Analysis of TP2 Copper Helical Pipe
摘 要
采用宏观观察、化学成分分析、扫描电镜断口观察及显微组织检验等方法对出现裂纹的TP2铜螺旋管进行了分析。结果表明：多次冷变形使铜管处于加工硬化状态,内应力集中于肋片部位而导致裂纹产生。并提出了改进措施。
化学成分
应力集中
裂纹
helical pipe
chemical composition
stress concentration
crack
Abstract
The macroscopic analysis,chemical composition analysis,SEM observation and metallographic examination were developed to analyze cracks of the TP2 copper helical pipe. The results showed that multiple deformations made the products in a work-hardening state during the cold forming,so internal stress concentrated in the fin-site lead to cracks. And the improved measures were also brought forward.
中图分类号 TG146.1+1
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/10/16
修改稿日期
网络出版日期
作者单位点击查看
备注尚延伟(1982-),男,助理工程师,学士。
引用该论文: SHANG Yan-wei,ZHAO Mei-chun,CHEN Wei-feng. Crack Analysis of TP2 Copper Helical Pipe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(3): 172～174
尚延伟,赵梅春,陈伟锋. TP2铜螺旋管裂纹产生原因分析[J]. 理化检验－物理分册, 2009, 45(3): 172～174
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙 智,江 利,应鹏展.失效分析基础与应用[M].北京:机械工业出版社,2005．
【2】颜 鹏,王玉霞.空拔管的纵裂与残余应力[J].钢管,1990(1):3-5．
【3】宁吉仁.T2挤压管表面微观裂纹产生的原因及解决途径[J].铜加工,1992(1):144-145．
【2】颜 鹏,王玉霞.空拔管的纵裂与残余应力[J].钢管,1990(1):3-5．
【3】宁吉仁.T2挤压管表面微观裂纹产生的原因及解决途径[J].铜加工,1992(1):144-145．
相关信息