Defects in Laser Remelting Layer of AZ91D Magnesium Alloy
摘 要
以AZ91D镁合金为研究对象,研究激光熔凝镁合金的工艺特点,分析熔凝层中出现的常见缺陷,并探讨其产生的主要原因。结果表明: 气孔、裂纹和夹杂是AZ91D镁合金激光熔凝层中存在的主要缺陷。但只要熔凝过程中工艺参数选择合适,这些缺陷是可以避免或减少的。
Abstract
The technology characteristic of magnesium alloy after laser remelting and the common defects in the solidifying layer were studied. The prime reasons which bring microstructure defection were discussed also. The results show that the primary defects in solidifying layer of AZ91D magnesium alloy are gas cavity,crack and inclusion. These defects can be avoided or decreased if only the technology parameters are selected in reason during remelting process.
中图分类号 TG166.4
所属栏目 试验与研究
基金项目 吉林省教育厅资助项目(吉教科合字[2006]第70号)
收稿日期 2008/5/26
修改稿日期
网络出版日期
作者单位点击查看
备注赵 宇(1968-),男,博士,副教授。
引用该论文: ZHAO Yu,CUI Zhen-yu,CHEN Li,ZHAO Jing. Defects in Laser Remelting Layer of AZ91D Magnesium Alloy[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(4): 202~204
赵 宇1,2,崔振宇1,陈 莉1,赵 静1. AZ91D镁合金激光熔凝层的缺陷[J]. 理化检验-物理分册, 2009, 45(4): 202~204
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张光钧. 激光热处理的现状及发展[J]. 金属热处理,2000(1): 6-11.
【2】李俊昌,李行一,陈庆华. 激光热处理中实际光束热作用的快速分析[J]. 材料研究学报,1998,12(3):262-266.
【3】YILBAS B S. Laser melting of plasma nitrided Ti-6Al-4V alloy[J]. Wear,1998,214:140-149.
【4】MAJUMDARI J D,MISHRA P,DAS D,et al. Studies of defects in laser surface treated magnesium and its alloy[J]. Laser in Engineering,2004,14(3/4):193-211.
【5】WANG A H,YUE T M. Surface characteriststic change of SiC reinforced Mg-alloy composite induced by excimer laser surface treating[J].J Mater Sci Lett ,2001,20(21):1965-1967.
【6】马怀宪. 金属塑性加工学[M]. 北京: 冶金工业出版社,1997: 38-44.
【2】李俊昌,李行一,陈庆华. 激光热处理中实际光束热作用的快速分析[J]. 材料研究学报,1998,12(3):262-266.
【3】YILBAS B S. Laser melting of plasma nitrided Ti-6Al-4V alloy[J]. Wear,1998,214:140-149.
【4】MAJUMDARI J D,MISHRA P,DAS D,et al. Studies of defects in laser surface treated magnesium and its alloy[J]. Laser in Engineering,2004,14(3/4):193-211.
【5】WANG A H,YUE T M. Surface characteriststic change of SiC reinforced Mg-alloy composite induced by excimer laser surface treating[J].J Mater Sci Lett ,2001,20(21):1965-1967.
【6】马怀宪. 金属塑性加工学[M]. 北京: 冶金工业出版社,1997: 38-44.
相关信息