飞机操纵系统链条销轴断裂分析
Failure Analysis of Chain Pin Shaft in Aero Navigating System
摘 要
某型飞机操纵系统链条销轴在使用中断裂。采用化学成分分析、外观检查、断口分析和表面质量检验等方法对断裂销轴进行了分析，又对有裂纹的销轴与断裂销轴进行了对比分析。结果表明: 销轴表面存在原始缺陷,加上链条链板在长期使用中的磨损使得链板间隙增大,导致销轴承受剪切力的同时又承受弯曲载荷,最终导致销轴发生疲劳断裂。
链条销轴
疲劳断裂
磨损
aero navigating system
chain pin shaft
fatigue fracture
wear
Abstract
Chain pin shaft in one aero navigating system were fractured in service. A cracked pin shaft and a fractured one were analyzed,through visual inspection,fracture analysis and presentation quality check. The results showed that there existed original defects in the pin shaft surface,and the pin shaft bore bend and shear load which wear of chain plates during long-term service enlaryed the dearomce of the plates,original defects and wear of chain plates caused the chain pin shaft fatigure failure.
中图分类号 V227
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/11/23
修改稿日期
网络出版日期
作者单位点击查看
备注李 权(1974-),男,工程师。
引用该论文: LI Quan,XU Zhi-gang,ZHANG Dong,CHEN Rong,FU Guo-ru. Failure Analysis of Chain Pin Shaft in Aero Navigating System[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(4): 217～220
李 权,徐志刚,张 栋,陈 荣,傅国如. 飞机操纵系统链条销轴断裂分析[J]. 理化检验－物理分册, 2009, 45(4): 217～220
被引情况:
【1】丛建臣,孙军,于晓东,倪培相,邵诗波, "C70S6钢连杆疲劳试验过早开裂原因分析",理化检验－物理分册 51, 501-503(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】航空制造工程手册总编委会主编.航空制造工程手册表面处理[M].北京: 航空工业出版社,1993:217-222．
【2】郑修麟.材料的力学性能[M]. 西安: 西北工业大学出版社,2000:60-96．
【3】张栋,钟培道,陶春虎,等.失效分析[M].北京: 国防工业出版社,2004:135．
【4】张启军. 浅谈链条零件的选用及其热处理[J].国外金属热处理,2003,24(6):40-41．
【2】郑修麟.材料的力学性能[M]. 西安: 西北工业大学出版社,2000:60-96．
【3】张栋,钟培道,陶春虎,等.失效分析[M].北京: 国防工业出版社,2004:135．
【4】张启军. 浅谈链条零件的选用及其热处理[J].国外金属热处理,2003,24(6):40-41．
相关信息