摘 要
利用金相检验、X射线衍射、光电子能谱、直读光谱、硬度和密度测试等方法对国外某型高速楔块式离合器的楔块未知材料试样进行检测分析。综合检测数据确定楔块基体材料为GCr15,并经淬火处理,硬度均匀,楔块表面有6.8～8.3 μm的渗铬层。该楔块具有良好的耐磨性和抗蚀性。
楔块
金相检验
X射线衍射
能谱
clutch
wedge
metallographic examination
X-ray diffraction
energy spectroscopy
Abstract
By means of metallographic examination,X-ray diffraction,X-ray photoelectron spectroscopy,hardness and density testing,etc.,the wedge unknown material of a high speed overrunning clutch was analyzed. With comprehensive analysis to the testing results,the sample material was determined as GCr15. The testing also showed that the material was quench-hardened,and the chromized layer with depth of 6.8-8.3 μm on sample surface raised wear resistance and corrosion resistance of the material.
中图分类号 TH142.2
所属栏目 试验技术与方法
基金项目
收稿日期 2008/12/29
修改稿日期
网络出版日期
作者单位点击查看
备注李 强(1975-),男,工程师，硕士。
引用该论文: LI Qiang,REN Dong,LUO Rui,LI Ping-hua,LONG Hua. Inspection Analysis on Imported Clutch Wedge Material[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(5): 282～284
李 强,任 东,骆 锐,李平化,龙 华. 进口离合器楔块材料的检测[J]. 理化检验－物理分册, 2009, 45(5): 282～284
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】谈育煦,胡志忠. 材料研究方法[M]. 北京: 机械工业出版社,2004．
【2】李风,靳兰芬,于黎佳.金相显微镜与计算机图形处理技术[J]. 理化检验(物理分册),2000,36(2):81-82．
【3】刘粤惠,刘平安.X射线衍射分析原理与应用[M]. 北京:化工出版社,2003．
【4】邱丽美,刘芬,赵良仲.样品表面污染对X射线光电子能谱定量分析的影响[J]. 理化检验(化学分册),2007,43(3):182-184．
【5】刘青松.用光谱仪检测材料元素时的注意事项[J].理化检验(物理分册),2007,43(3):159 ．
【6】GB/T 4340.1-1999 金属维氏硬度试验 第1部分：试验方法[S]．
【2】李风,靳兰芬,于黎佳.金相显微镜与计算机图形处理技术[J]. 理化检验(物理分册),2000,36(2):81-82．
【3】刘粤惠,刘平安.X射线衍射分析原理与应用[M]. 北京:化工出版社,2003．
【4】邱丽美,刘芬,赵良仲.样品表面污染对X射线光电子能谱定量分析的影响[J]. 理化检验(化学分册),2007,43(3):182-184．
【5】刘青松.用光谱仪检测材料元素时的注意事项[J].理化检验(物理分册),2007,43(3):159 ．
【6】GB/T 4340.1-1999 金属维氏硬度试验 第1部分：试验方法[S]．
相关信息