拉伸试验的速率探讨
Discussion on Rate of Tensile Test
摘 要
采用夹头分离速率控制方式对有屈服现象和无屈服现象的试样进行拉伸试验,探讨了试验过程中试样应变速率和应力速率的变化情况。试验结果表明:在不同的变形阶段试样的应变速率是不同的,弹性阶段的应变速率比设定值低很多,屈服阶段会略高,塑性变形阶段与设定值较接近。并确定在该试验条件下可将试验速率设定在1~7 mm/min。
应变速率
刚度
拉伸试验
grip separate rate
strain rate
stiffness
tensile test
Abstract
The change of strain rate and stress rate of samples with and without yielding phenomenon was studied during the tensile test under the control of grip separate rate. It is showed that strain rate was different in the different deformation stage,the value of strain rate was much lower than the set value in elastic stage,little higher in yield,and close to the set value in the plastic deformation. And the test rate was enacted in 1-7 mm/min under the testing condition.
中图分类号 TG115.5+2
所属栏目 试验技术与方法
基金项目
收稿日期 2008/11/24
修改稿日期
网络出版日期
作者单位点击查看
备注陈华锋(1983-),男,硕士研究生。
引用该论文: CHEN Hua-feng,WANG Bin,HUANG Xu-dong. Discussion on Rate of Tensile Test[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(5): 285～287
陈华锋,王 滨,黄旭东. 拉伸试验的速率探讨[J]. 理化检验－物理分册, 2009, 45(5): 285～287
被引情况:
【1】董强,宰绍峰,孙建林,刘明, "GB/T 228.1-2010中的拉伸试验速率及其控制",理化检验－物理分册 47, 774-781(2011)
【2】张有为,乔建军,任学平, "拉伸速率控制模式及拉伸速率对冷轧薄板强度测试结果的影响",理化检验－物理分册 49, 233-235(2013)
【3】岑风,陈益华,张珂, "金属材料室温拉伸试验新旧国家标准的对比分析",理化检验－物理分册 48, 804-807(2012)
【4】张万松,王建国, "浅析金属材料室温拉伸试验方法变更后的证实",理化检验－物理分册 49, 310-313(2013)
【5】孙绍广,于秀娥,苏洪英,吕丹,陈洪凯,王超逸, "拉伸试验速率控制模式及试验速率的选择",理化检验－物理分册 49, 497-500(2013)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 228-2002 金属材料 室温拉伸试验方法[S]．
相关信息