空压机ZR750低压机头LP转子驱动齿轮断裂分析

Fracture Analysis of Gear Driven LP Rotor in ZR750 Compressor Low-pressure Nose

田虹

摘要

通过对空压机ZR750低压机头LP转子驱动齿轮断裂部位进行理化检测和分析,推断其失效原因为在机器发生故障后仍反复强行运转,致使承受很大的冲击和弯曲应力,导致在应力集中的齿轮齿根部位产生了断裂。

标签齿轮

啮合面

弯曲疲劳

接触疲劳

应力集中

断裂

gear

action surface

bending fatigue

contact fatigue

stress concentration

fracture

Abstract

Through the physical and chemical analysis of the fracture of gear driven LP rotor in ZR750 compressor low-pressure nose,the results showed that the failure reason was the repeatedly forced operation after machine fault. It made gear under enormous impact and bending stress,and then the fracture happened in the stress concentration area of the root of gear.

中图分类号 TE92

所属栏目质量控制与失效分析

基金项目

收稿日期 2008/7/17

修改稿日期

网络出版日期

作者单位点击查看

备注田虹(1960-),女,工程师。

引用该论文: TIAN Hong. Fracture Analysis of Gear Driven LP Rotor in ZR750 Compressor Low-pressure Nose[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(5): 323～325
田虹. 空压机ZR750低压机头LP转子驱动齿轮断裂分析[J]. 理化检验－物理分册, 2009, 45(5): 323～325

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】谢建欣，王伟志.标准金相图谱与最新热处理技术标准第三卷[M]. 北京：新星出版社,2006: 1234．

【2】任颂赞. 钢铁金相图谱[M]. 上海：科学技术文献出版社,2003:792．

【3】陶达天. 金相检验实例[M]. 北京：机械工业出版社,1975:141．

相关信息

	标题	相关频次
	无缝钢管生产用芯棒断裂失效分析	6
	变速器中间轴齿轮断裂分析	5
	10.9级螺栓早期疲劳断裂失效分析	4
	40Cr钢齿轴的断裂原因分析	4
	IEU钻杆刺穿断裂原因分析	4
	ZG15Cr2Mo1合金铸件吊耳断裂原因分析	4
	柴油机用高强度螺栓断裂失效分析	4
	车轮锻压模具用下芯棒断裂原因	4
	沉头铆钉断裂原因分析	4
	川渝地区某气井钻铤断裂原因	4
	导弹发射装置锁制机构失效分析	4
	电厂外供泵轴断裂原因分析	4
	电动后桥壳断裂原因	4
	电机轴断裂原因分析	4
	电流互感器引流抱箍线夹断裂原因	4
	分动箱齿轮断裂原因	4
	核电厂循环水泵盘根压盖螺栓断裂原因	4
	恒速传动装置齿轮断裂失效分析	4
	马蹄形卸扣断裂原因分析	4
	某HL级35CrMo抽油杆断裂原因分析	4
	某产线变速箱齿轮断裂原因	4
	某钢结构螺栓断裂失效分析	4
	某高温重载自润滑关节轴承超载试验失效原因分析	4
	某井油管断裂原因分析	4
	凝结水泵轴断裂原因分析	4
	气瓶瓶阀断裂原因	4
	燃气轮发电机导电螺钉的断裂原因分析	4
	十字万向关节断裂原因分析	4
	质量控制与失效分析9FA燃机过渡段用螺栓断裂分析	4
	自动扶梯扶手驱动轴断裂原因分析	4