Cracking Analysis of Importation B70 Grade Line Welding Pipe in Cold-bend Test
摘 要
对在冷弯试验中焊缝开裂的进口B70级直缝焊管进行了金相检验、焊缝断口形貌分析以及夹杂物成分分析。结果表明：焊缝中分布在铁素体晶界上的渗碳体以及焊缝中存在的夹杂物和气孔是导致冷弯试验中发生开裂的主要原因。
气孔
渗碳体
inclusion
gas porosity
cementite
Abstract
Metallurgical analysis,fracture analysis and chemical composition analysis were carried out on the B70 grade line welding pipe which cracked during the cold bending test. The results showed that network cementite distributing along the boundary of ferrite grains,inclusions and gas porosities caused the cracking of pipe during the cold bending test.
中图分类号 TK172.4
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/5/12
修改稿日期
网络出版日期
作者单位点击查看
备注朱锦波(1981-),男,助理工程师。
引用该论文: ZHU Jin-bo,FU Zhi-qiang,YAO Jiu-hong. Cracking Analysis of Importation B70 Grade Line Welding Pipe in Cold-bend Test[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(6): 361～363
朱锦波,傅志强,姚久红. 进口B70级直缝焊管冷弯试验开裂分析[J]. 理化检验－物理分册, 2009, 45(6): 361～363
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】ASTM A672中温高压用电熔焊钢管[S]．
【2】ASTM A515中高温压力容器用碳素钢板[S]．
【3】ASTM A370钢制品机械测试的标准试验方法和定义[S]．
【4】邱葭菲. 20 g埋弧自动焊焊接接头冷弯开裂的研究[J]. 现代制造工程,2003(11)：46-47．
【5】刘辉义. 20钢无缝化ERW焊管生产中产生焊缝横向开裂的原因分析[J]. 焊管,2007,30(4)：66-68．
【2】ASTM A515中高温压力容器用碳素钢板[S]．
【3】ASTM A370钢制品机械测试的标准试验方法和定义[S]．
【4】邱葭菲. 20 g埋弧自动焊焊接接头冷弯开裂的研究[J]. 现代制造工程,2003(11)：46-47．
【5】刘辉义. 20钢无缝化ERW焊管生产中产生焊缝横向开裂的原因分析[J]. 焊管,2007,30(4)：66-68．
相关信息