Fracture Reason Analysis of GCr15 Bearing Steel Continuous Casting Billet
摘 要
采用化学成分分析、宏观和微观检验等方法对GCr15轴承钢连铸坯在步进式加热炉内加热过程中发生断裂的原因进行了分析。结果表明:断坯中存在较多沿奥氏体晶界分布的网状裂纹,晶界呈熔凝特征,晶界上有许多含硅、铝、铬和锰等的液滴状复合氧化物颗粒,断口附近的沿晶裂纹周围氧化脱碳严重,局部有粗大魏氏组织。这些特征表明加热炉局部存在温度过高现象,进而导致坯料晶界弱化,并且在坯料和步进梁构成的悬臂拉力作用下最终造成沿晶断裂。
Abstract
The fracture reason of GCr15 bearing steel continuous casting billet burned in working beam furnace had been analyzed by means of chemical composition analysis,macro and microstructure test. Results showed that much pattern cracking,around which severe oxidize and decarburized structure and little coarse widmanstatten structure were found,distributed along austenite grain boundaries that had obvious fused feature and were inlayed by some gutta multiple oxide particle with the composition of Si,Al,Cr and Mn elements. The fracture of the billet was caused by overburning with high temperature in certain local area of the furnace which led to grain boundary weakness and then formed intercrystalline cracking with the pulling force between ingot and walking beam.
中图分类号 TG142.41
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/9/17
修改稿日期
网络出版日期
作者单位点击查看
备注范植金(1963-),男,高级工程师。
引用该论文: FAN Zhi-jin,ZHANG You-deng,YAN Xiang,LUO Guo-hua. Fracture Reason Analysis of GCr15 Bearing Steel Continuous Casting Billet[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(7): 431~433
范植金,张友登,严 翔,罗国华. GCr15轴承钢连铸坯断裂原因分析[J]. 理化检验-物理分册, 2009, 45(7): 431~433
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】HEIM S A. 防止锻钢轧辊的过热和过烧[J]. 轧钢,1991,8(2):11-12.
相关信息