海水泵叶轮叶片的断裂分析
Fracture Analysis of Sea Water Pump Impeller Vane
摘 要
海水泵使用两个月即发生叶轮叶片断裂事故。采用化学成分分析、力学性能测试及金相检验等方法对其断裂原因进行了分析。结果表明：由于海水泵叶片本身存在大量的铸造孔洞及疏松等缺陷，在交变载荷的作用下产生裂纹失稳扩展直至产生疲劳断裂。建议提高海水泵叶轮部件铸造质量。
叶轮
叶片
铸造缺陷
sea water pump
impeller
vane
casting defect
Abstract
The impeller vane of sea water pump was fractured just after two months. The fracture reason was analyzed by chemical composition analysis,mechanical property test and metallographic examination. The results showed that the fracture occurred under cyclic loading because of the casting hole and rarefaction in vane. It was proposed that the casting quality of the sea water pump impeller sould be improved.
中图分类号 TH38
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/10/6
修改稿日期
网络出版日期
作者单位点击查看
备注吴继权(1968-),男,工程师，博士。
引用该论文: WU Ji-quan,ZHOU Xu-nan,ZHANG Ju-guang. Fracture Analysis of Sea Water Pump Impeller Vane[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(7): 443～445
吴继权,周旭南,张居光. 海水泵叶轮叶片的断裂分析[J]. 理化检验－物理分册, 2009, 45(7): 443～445
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】海交通大学．金属断口分析[M]. 北京：国防工业出版社，1979：210-214．
【2】GB/T 2100-2002 一般用途耐蚀钢铸件[S]．
【3】胡世炎. 破断故障金相分析[M]. 北京：国防工业出版社，1979：280-282．
【4】张栋，钟培道. 失效分析[M]. 北京：国防工业出版社，2005：198-206．
【5】吴连生. 失效分析技术及其应用——第二讲 断裂分类及韧、脆断裂的转变[J]. 理化检验-物理分册，1995，31(6)：57-61．
【6】曹力军. 主轴断裂分析[J].理化检验-物理分册，2007，37(12)：539-541．
【2】GB/T 2100-2002 一般用途耐蚀钢铸件[S]．
【3】胡世炎. 破断故障金相分析[M]. 北京：国防工业出版社，1979：280-282．
【4】张栋，钟培道. 失效分析[M]. 北京：国防工业出版社，2005：198-206．
【5】吴连生. 失效分析技术及其应用——第二讲 断裂分类及韧、脆断裂的转变[J]. 理化检验-物理分册，1995，31(6)：57-61．
【6】曹力军. 主轴断裂分析[J].理化检验-物理分册，2007，37(12)：539-541．
相关信息