发动机启动发电机弹性轴断裂分析
Fracture Analysis of Flexible Shaft of Engine Starter-generator
摘 要
通过硬度检验、断口分析和金相检验等方法,确认断裂的发动机启动发电机弹性轴为扭转疲劳断裂失效,弹性轴锥体和衬套间配合松动导致的反复冲击是其断裂失效的关键因素,键槽设计的深度较大和加工质量粗糙进一步增大了转角处的应力水平,促进了裂纹萌生。
冲击载荷
扭转疲劳
键槽结构
flexible shaft
impact load
torsion fatigue
keyslot configuration
Abstract
The flexible shaft of engine starter-generator was analyzed through hardness test,fracture analysis and metallography examination. The results showed that the fracture mode of the flexible shaft was torsion fatigue. The iterative impact load which was mainly due to the flexible shaft cone and bush cone cooperate become flexible was the key factor. The stress lever of striking angle was more increased because of keyslot configuration and machining quality which accelerate initiation of crack.
中图分类号 U233.3+22
所属栏目 质量控制与失效分析
基金项目 无损检测技术教育部重点实验室开放基金(ZD200729011)
收稿日期 2009/4/8
修改稿日期
网络出版日期
作者单位点击查看
备注胡春燕(1983-),女,硕士研究生。
引用该论文: HU Chun-yan,LI Ying,TAO Chun-hu,LI Ming,LIU Xin-ling. Fracture Analysis of Flexible Shaft of Engine Starter-generator[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(7): 448～450
胡春燕,李 莹,陶春虎,黎 明,刘新灵. 发动机启动发电机弹性轴断裂分析[J]. 理化检验－物理分册, 2009, 45(7): 448～450
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】《中国航空材料手册》编辑委员会.航空材料手册[M]. 北京：中国标准出版社,2002．
【2】路兰英.启动发电机软轴断裂分析[J]. 材料工程,2003(增刊):100-103．
【3】《常用结构钢金相图谱》编写组.常用结构钢金相图谱[M]. 上海：上海科学技术文献出版社,1982．
【4】张栋,钟培道,陶春虎,等. 失效分析[M]. 北京：国防工业出版社,2004．
【5】陶春虎,习年生,钟培道,等. 航空装备失效典型案例分析[M]. 北京：国防工业出版社,1998．
【2】路兰英.启动发电机软轴断裂分析[J]. 材料工程,2003(增刊):100-103．
【3】《常用结构钢金相图谱》编写组.常用结构钢金相图谱[M]. 上海：上海科学技术文献出版社,1982．
【4】张栋,钟培道,陶春虎,等. 失效分析[M]. 北京：国防工业出版社,2004．
【5】陶春虎,习年生,钟培道,等. 航空装备失效典型案例分析[M]. 北京：国防工业出版社,1998．
相关信息