127 mm S135钻杆刺漏失效分析
Piercing Failure Analysis of 127 mm S135 Drill Pipe
摘 要
采用宏观分析、化学成分分析、金相检验、断口分析和力学性能检测等方法并结合钻杆的受力和环境工况对127 mm S135钻杆管体发生刺漏失效的原因进行了分析。结果表明：钻杆的刺漏失效形式为腐蚀疲劳失效;钻杆外表面存在腐蚀坑，在交变应力的恶劣工况作用下于腐蚀坑底部萌生疲劳裂纹并扩展,最终发生刺漏失效。
刺漏
失效分析
腐蚀疲劳
drill pipe
piercing
failure analysis
corrosion fatigue
Abstract
By means of macroscopic examination,chemical composition analysis,microstructure examination and mechanical properties test on the material,combined with the use condition and load analysis,the piercing failure of a 127 mm S135 drill pipe were analyzed. The results show that it was the corrosion pits with stress concentration at the outer surface of drill pipe and the alternating stress,that resulted in the fatigue crack initiation and expansion quickly at the bottom of pits.
中图分类号 TE921+.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/3/13
修改稿日期
网络出版日期
作者单位点击查看
备注叶顶鹏(1973-),男,工程师。
引用该论文: YE Ding-peng,WANG Rui-cheng,CUI Shun-xian,LIAO Ling,YUAN Zhong-hua. Piercing Failure Analysis of 127 mm S135 Drill Pipe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(8): 514～516
叶顶鹏,王瑞成,崔顺贤,廖凌,袁中华. 127 mm S135钻杆刺漏失效分析[J]. 理化检验－物理分册, 2009, 45(8): 514～516
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘永刚,叶顶鹏. 对现行钻杆标准技术条款的分析研究[J]. 石油机械,2008,36(9):179-181．
【2】章扬烈. 钻柱运动学与动力学[M]. 北京：石油工业出版社,2001．
【2】章扬烈. 钻柱运动学与动力学[M]. 北京：石油工业出版社,2001．
相关信息