水泵用密封件的失效分析
Failure Analysis of Seal Element for Water Pump
摘 要
离子渗氮后的40Cr钢水泵用动态密封件在使用过程中因变形而破裂。采用金相检验与显微硬度测定的方法对该零件进行了分析。结果表明: 导致零件失效的主要原因是渗氮后零件的硬度太低,渗氮层深度较浅所致。并提出了相应的建议。
密封件
离子渗氮
渗氮层
显微组织
显微硬度
water pump
seal element
ion nitriding
nitrided layer
microstructure
microhardness
Abstract
Dynamic seal element used for water pump made by 40Cr steel treated through ion nitriding process distorted and broke in use. The element was analyzed by means of metallographic examination and microhardness measurement. The result showed that the microhardness was too low and the nitrided layer was too shallow after nitriding process. Some suggestion was presented to increase the life of the element.
中图分类号 TH136
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/2/18
修改稿日期
网络出版日期
作者单位点击查看
备注李传瑞(1971-),男,讲师,硕士。
引用该论文: LI Chuan-rui,DING Li. Failure Analysis of Seal Element for Water Pump[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(9): 573～574
李传瑞,丁 丽. 水泵用密封件的失效分析[J]. 理化检验－物理分册, 2009, 45(9): 573～574
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】安运铮. 热处理工艺学[M]. 北京: 机械工业出版社,1989: 210-221．
【2】夏立芳. 金属热处理工艺学[M]. 哈尔滨: 哈尔滨工业出版社,2006: 164-166．
【2】夏立芳. 金属热处理工艺学[M]. 哈尔滨: 哈尔滨工业出版社,2006: 164-166．
相关信息