T23高温再热器管爆管原因分析
Leakage Analysis of T23 Steel High Temperature Reheater Tube
摘 要
通过宏观形貌分析、化学成分分析、拉伸试验、金相检验和理论计算等方法对在我国较早应用在电厂锅炉高温再热器的T23钢管的爆管原因进行了分析。结果表明：管子外壁氧化腐蚀减薄是导致T23再热器管爆管的主要原因,因爆管附近烟温偏高而导致的管子材料显微组织老化和性能劣化对再热器管爆管起促进作用。
高温再热器
爆管
氧化腐蚀
T23 steel pipe
high temperature reheater
leakage
oxide corrosion
Abstract
Leakage reason of T23 steel tube in high temperature reheater was researched through a set of tests of macro check,tensile test,microstructure examination and theoretical calculation. The results show that the main reason for the leakage was due to oxide corrosion which resulted in the reduction of the tube’s wall thickness. Microstructure aging and mechanical deterioration of the tube caused by higher fuel gas temperature near the leaked tube accelerated the leakage.
中图分类号 TG113
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/3/2
修改稿日期
网络出版日期
作者单位点击查看
备注刘树涛(1959-),男,河北盐山人，研究员，主要从事电站金属材料等方面的研究。
引用该论文: LIU Shu-tao,SHI Zhi-gang,LU Jun,TANG Li-ying,LIANG Feng. Leakage Analysis of T23 Steel High Temperature Reheater Tube[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(10): 638～641
刘树涛,史志刚,陆 军,唐丽英,梁 锋. T23高温再热器管爆管原因分析[J]. 理化检验－物理分册, 2009, 45(10): 638～641
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】范如杞,王智峰. CASE2199钢焊接技术试验研究[J]. 电焊机,2003,33(10)：44-45．
【2】金科,聂铭,范振宁,等. T23钢管材老化性能评估[J]. 广东电力,2007,20(2)：44-47．
【3】王起江,邹凤鸣,赵群义,等. 宝钢T23高压锅炉管的研制[J]. 宝钢技术,2006(1)：59-62．
【4】DL 438-2000 火力发电厂金属技术监督规程[S]．
【5】GB/T 9222-2008 水管锅炉受压元件强度计算[S]．
【6】DL/T 654-2009 火电机组寿命评估技术导则[S]．
【7】岑可法,樊建人. 锅炉和热交换器的积灰、结渣、磨损和腐蚀的防止原理与计算[M]. 北京：科学出版社.1994．
【8】王杏卿. 热力设备的腐蚀与防护[M]. 北京：水利电力出版社. 1988: 212-214．
【2】金科,聂铭,范振宁,等. T23钢管材老化性能评估[J]. 广东电力,2007,20(2)：44-47．
【3】王起江,邹凤鸣,赵群义,等. 宝钢T23高压锅炉管的研制[J]. 宝钢技术,2006(1)：59-62．
【4】DL 438-2000 火力发电厂金属技术监督规程[S]．
【5】GB/T 9222-2008 水管锅炉受压元件强度计算[S]．
【6】DL/T 654-2009 火电机组寿命评估技术导则[S]．
【7】岑可法,樊建人. 锅炉和热交换器的积灰、结渣、磨损和腐蚀的防止原理与计算[M]. 北京：科学出版社.1994．
【8】王杏卿. 热力设备的腐蚀与防护[M]. 北京：水利电力出版社. 1988: 212-214．
相关信息