45钢厚板弯曲开裂原因分析
FRACTURE ANALYSIS OF THE 45 STEEL PLATE IN BENDING
摘 要
45钢厚板在弯曲时发生断裂，对断裂钢板进行了化学成分分析和宏、微观检验。认为板材在铆焊气割时,加热不均匀，局部过热且冷却速度过快，产生了粗大的魏氏组织，加之沿晶三次渗碳体的存在，使材质变脆；同时产生较大的内应力，使钢板生成微裂纹，造成弯卷过程中开裂。
断裂
内应力
魏氏组织
45 Steel plate
Fracture
Internal stress
Widmanstatten structure
Abstract
The fracture of 45 steel plate was analyzed by means of macrocosmic and microcosmic. The results showed that the fracture and crack of 45 steel plate was caused by internal stress when gas cutting; asymmetry heat make plate partly and cooling rate excessive rapidness wastcausing widmanstatten structure, and thrice cementite producing along the grain edge. All that badness microcosmic structure make nature of material became brittleness, and crack when bending.
中图分类号 TG142.41
所属栏目
基金项目 安徽省教委资助(2005KJ039ZD)
收稿日期 2004/11/12
修改稿日期
网络出版日期
作者单位点击查看
备注钱健清(1963-),男，副教授，硕士。
引用该论文: QIAN Jian-qing,LUO Xiu-mei,ZHANG Fong. FRACTURE ANALYSIS OF THE 45 STEEL PLATE IN BENDING[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(2): 97～99
钱健清,罗透梅,张峰. 45钢厚板弯曲开裂原因分析[J]. 理化检验－物理分册, 2006, 42(2): 97～99
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王红梅,张 艳.50钢板裂纹分析[J].物理测试, 2003,39(4):33-35.
【2】蔡 红,员丽京.齿轮轴裂纹分析[J].理化检验-物理分册, 2003,39(11):593-594.
【3】刘 毅主编.金属学与热处理[M].北京:冶金出版社, 1995.
【4】[英]F布赖恩,皮克林主编.钢的组织与性能[M].北京:科学出版社, 1999.
【2】蔡 红,员丽京.齿轮轴裂纹分析[J].理化检验-物理分册, 2003,39(11):593-594.
【3】刘 毅主编.金属学与热处理[M].北京:冶金出版社, 1995.
【4】[英]F布赖恩,皮克林主编.钢的组织与性能[M].北京:科学出版社, 1999.
相关信息