不锈钢换热器板片泄漏原因分析
LEAK ANALYSIS ON STAINLESS STEEL RADIATOR BOARD
摘 要
316不锈钢换热器板片在使用中发生泄漏。对失效件进行了金相检验、腐蚀产物的成分分析，以及应力状态分析，对腐蚀起主要作用的氯离子的来源，以及氯离子在应力腐蚀过程中循环作用的机理作了探讨。结果表明，该换热器板片泄漏为应力腐蚀所致。
孪晶奥氏体
穿晶
滑移
Stress-corrosion
Twin austenite
Transgranular
Slip
Abstract
The leak reason of 316 stainless steel radiator board was stress corrosion according to the results of metallographic examnation, chemical compositon ananlysis of the corrosive product and stress state analysis of failure specimen. Stress corrosion mechanisms was discussed. The source of Cl- responsible for the corrosion mainly and cyclical reaction mechanisms of Cl- during the stress corrosion process of stainless steel were studied in detail.
中图分类号 TG142.71
所属栏目
基金项目
收稿日期 2005/7/8
修改稿日期
网络出版日期
作者单位点击查看
备注王荣(1966-)，男，高级工程师，学士。
引用该论文: WANG Rong. LEAK ANALYSIS ON STAINLESS STEEL RADIATOR BOARD[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(5): 255～257
王荣. 不锈钢换热器板片泄漏原因分析[J]. 理化检验－物理分册, 2006, 42(5): 255～257
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】任赞颂,张静江.钢铁金相图谱[M].上海:上海科学技术文献出版社, 2003.864.
【2】John Sedriks A.不锈钢的腐蚀[M].北京:机械工业出版社, 1986.
【3】张静江.不锈钢管应力腐蚀开裂失效分析[A].第三界全国失效分析会议论文集[C].上海:上海材料研究所出版, 1988.
【2】John Sedriks A.不锈钢的腐蚀[M].北京:机械工业出版社, 1986.
【3】张静江.不锈钢管应力腐蚀开裂失效分析[A].第三界全国失效分析会议论文集[C].上海:上海材料研究所出版, 1988.
相关信息