弹簧断裂原因分析
ANALYSIS OF THE SPRING FRACTURE REASONS
摘 要
弹簧在弹栓试验时发生断裂。采用化学成分分析、金相检验和扫描电镜分析等手段，对断裂弹簧进行了分析。结果表明，弹簧在去氢时未严格按工艺要求执行，致使大量的氢残留并呈弥散分布形态，进而形成沿晶裂纹。在外力作用下，导致沿晶脆性断裂。
断裂
氢脆
Spring
Fracture
Hydrogen embrittlement
Abstract
The springs fracture during the test of play to bolt. The means, such as chemical composition analysis, metallography and scanning eletron mircroscope etc, were used to analyse the springs. The result indicated: During removing hydrogen after cadmium plating the springs did not strictly execute technology, keeping a large amount of remanent hydrogen and dispersive distribution in the springs, and initiating crack along the grain boundary, which caused brittle fracture among grain boundary under applied force finally.
中图分类号 TH135
所属栏目
基金项目
收稿日期 2005/5/16
修改稿日期
网络出版日期
作者单位点击查看
备注韩晶(1963-)，女，工程师。
引用该论文: HAN Jing,XU Wei. ANALYSIS OF THE SPRING FRACTURE REASONS[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(5): 258～260
韩晶,徐巍. 弹簧断裂原因分析[J]. 理化检验－物理分册, 2006, 42(5): 258～260
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】桂立丰,唐汝钧.机械工程材料测试手册(物理金相卷)[M].沈阳:辽宁科学技术出版社, 1999.11.
【2】张英会,刘辉航,王德成.弹簧手册[M].北京:机械工业出版社, 2000.7.
【3】宋余九,荀毓闽.热处理手册(热处理质量控制和检验)[M].北京:机械工业出版社, 2001.7.
【4】上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社, 1987.7.
【2】张英会,刘辉航,王德成.弹簧手册[M].北京:机械工业出版社, 2000.7.
【3】宋余九,荀毓闽.热处理手册(热处理质量控制和检验)[M].北京:机械工业出版社, 2001.7.
【4】上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社, 1987.7.
相关信息