集装箱旋转锁轴失效分析
FAILURE ANALYSIS OF CONTAINER ROTATING LOCK AXLE
摘 要
铸钢锁轴在加工螺纹时轴杆端头断裂。对断裂件进行了化学成分和宏、微观分析，发现断裂锁轴的碳含量超标，并存在中心缩孔、严重区域偏析和局部共晶组织。据此对生产现场作了工序调查，发现浇注温度过高和直浇道欠浇是引起成分偏析及组织缺陷并导致断裂的主要原因。
理化检测
铸造工序分析
失效分析
Lock axis fracture
Physical testing and chemical analysis
Casting process analysis
Failure analysis
Abstract
Casting steel container rotating lock axle rod-head fracture in machining screw. Analysis was performed on the fracture by macroscopical, microscopical and chemical analysis methods.Failure is confirmed was caused by content higher carbon failure ,primare pipe, zone-segregation and eutectic ledeburit in lastly solidification. Working procedure causes were found out, poured short in sprue downgate and higher pour temperature is primary reason after investigating casting process in pouring house.
中图分类号 TH133.2
所属栏目
基金项目
收稿日期 2005/3/28
修改稿日期
网络出版日期
作者单位点击查看
备注徐益(1964-)，男，博士，副教授。
引用该论文: XU Yi,CHENG Li. FAILURE ANALYSIS OF CONTAINER ROTATING LOCK AXLE[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(8): 413～415
徐益,程里. 集装箱旋转锁轴失效分析[J]. 理化检验－物理分册, 2006, 42(8): 413～415
被引情况:
【1】郭全英,李启东,孙家仲,蔡淑芳,徐维良, "离合器拨叉失效分析",理化检验－物理分册 44, 44-47(2008)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王文清,李魁盛.铸造工艺学[M].北京:机械工业出版社, 1998.10.
【2】施廷藻.铸造实用手册[M].沈阳:东北工学院出版社, 1988.8.
【3】朱华栋.最新铸造标准实用手册[M].北京:兵器工业出版社, 1992.11.
【4】TB/T 2450-1993,铸钢非金属夹杂物技术条件[S].
【5】TB/T 1464-1991,铁道机车车辆用碳钢通用技术条件[S].
【6】陈国桢,肖柯则,姜不居.铸造缺陷和对策手册[M].北京:机械工业出版社, 2003.3.
【2】施廷藻.铸造实用手册[M].沈阳:东北工学院出版社, 1988.8.
【3】朱华栋.最新铸造标准实用手册[M].北京:兵器工业出版社, 1992.11.
【4】TB/T 2450-1993,铸钢非金属夹杂物技术条件[S].
【5】TB/T 1464-1991,铁道机车车辆用碳钢通用技术条件[S].
【6】陈国桢,肖柯则,姜不居.铸造缺陷和对策手册[M].北京:机械工业出版社, 2003.3.
相关信息