670t/h锅炉高温过热器管爆裂失效分析
FAILURE ANALYSIS ON A SUPERHEATER TUBE OF 670t/h BOILER
摘 要
某电厂1号锅炉的高温过热器在运行中发生爆漏。采用化学成分分析、宏观检验和显微组织分析等方法对爆管进行了分析；同时对爆管内壁氧化膜厚度的动态变化进行了测定，并以此来估算其当量温度，最后计算出剩余寿命。结果表明，过热器爆漏的原因是长期过热造成的。提出了预防措施。
高温过热器
爆漏
失效分析
Boiler
Superhearter
Leakage
Failure analysis
Abstract
The leakage failure of superheater happened in boiler No.1 of a power plant. Through chemical element analysis, macroscopic tests, microscopic metallographic analysis, and the quantitative measurement of the oxide scale on the inside-surface of the tube, in addition, by analyzing the thickness of the oxide scale on the inside-surface of the failed tube, the author evaluates the equivalent temperature and residual life time of the tube. Finally, the paper puts forward that the main reason leading to this failure is the long-term overheating of the tube. The preventive suggestions are also proposed.
中图分类号 TK223.3
所属栏目
基金项目
收稿日期 2006/3/23
修改稿日期
网络出版日期
作者单位点击查看
备注李正刚(1969-)，男，讲师，博士研究生。
引用该论文: LI Zheng-gang,LIAO Jin-zhi. FAILURE ANALYSIS ON A SUPERHEATER TUBE OF 670t/h BOILER[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(8): 425～427
李正刚,廖金枝. 670t/h锅炉高温过热器管爆裂失效分析[J]. 理化检验－物理分册, 2006, 42(8): 425～427
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】《火力发电厂金属材料料手册》编委会.火力发电厂金属材料料手册[M].北京:中国电力出版社, 2001.204-217.
【2】李金峰,欧阳杰.102钢高温再热器材质变化规律及寿命研究[J].河北电力技术, 1999,18(1):48-50.
【3】于显龙.锅炉管剩余寿命预测[J].发电设备, 1997,(11-12):74-75.
【2】李金峰,欧阳杰.102钢高温再热器材质变化规律及寿命研究[J].河北电力技术, 1999,18(1):48-50.
【3】于显龙.锅炉管剩余寿命预测[J].发电设备, 1997,(11-12):74-75.
相关信息