低压接管管线膨胀开裂原因分析
BULGE CRACKING ANALYSIS OF LOW-PRESSURE TAKE-OVER PIPELINES
摘 要
某低压乙二醇接管管线在运行过程中膨胀开裂。对爆管进行了宏微观检验、化学成分分析和厚度测试。结果表明，由于管段受到较大压力的作用，使管段产生较大的塑性变形，随着塑性变形的增大首先在接管焊缝热影响区的部位产生断裂破坏，最终导致爆管。提出了预防措施。
膨胀
开裂
失效分析
Low-pressure take-over pipelines
Bulging
Cracking
Failure analysis
Abstract
Bulging, cracking and fracture of low-pressure glycol take-over had been investigated by means of macroscopically ＆ microcosmic inspection, chemical composition analysis, thickness test, metallographic examination, scanning electrion microsope analysis. The results showed that the main reason of the take-over crack is owing to the pipelines fall under biggish stress, induce the take-over pipelines come into being biggish ductile distortion, go with this ductile distortion accretion, at the take-over welding line′s heat affected zone place appear rupture, finally bring cracking. After above analysis, the prevention measures are proposed.
中图分类号 TQ050.3
所属栏目
基金项目
收稿日期 2005/12/1
修改稿日期
网络出版日期
作者单位点击查看
备注田亚团(1980- )，男，助工，学士。
引用该论文: TIAN Ya-tuan. BULGE CRACKING ANALYSIS OF LOW-PRESSURE TAKE-OVER PIPELINES[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(9): 470～472
田亚团. 低压接管管线膨胀开裂原因分析[J]. 理化检验－物理分册, 2006, 42(9): 470～472
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘民治.失效分析的思路与诊断[M].北京:机械工业出版社, 1993.117.
【2】钟培道.断裂失效分析[J].理化检验-物理分册, 2005,41(7):375-378.
【3】黄淑菊.金属腐蚀与防护[M].西安:西安交通大学出版社, 1988.
【4】纪 贵.世界标准钢号手册[M].北京:中国标准出版社, 2003.
【5】林介东,钟万里,盘荣旋.燃煤锅炉水冷壁爆管原因分析[J].理化检验-物理分册, 2005,41(4):203-204.
【6】王宽福.焊接结构的塑性断裂失效与防治[J].石油工程建设, 1997,23(3):6-9.
【2】钟培道.断裂失效分析[J].理化检验-物理分册, 2005,41(7):375-378.
【3】黄淑菊.金属腐蚀与防护[M].西安:西安交通大学出版社, 1988.
【4】纪 贵.世界标准钢号手册[M].北京:中国标准出版社, 2003.
【5】林介东,钟万里,盘荣旋.燃煤锅炉水冷壁爆管原因分析[J].理化检验-物理分册, 2005,41(4):203-204.
【6】王宽福.焊接结构的塑性断裂失效与防治[J].石油工程建设, 1997,23(3):6-9.
相关信息